某高速铁路钢轨伤损原因分析
Reason Analysis on Defects in High-speed Railway Rail
摘 要
某城际高速铁路开通运营仅约半年, 使用的U71MnG 60 kg/m热轧钢轨在某车站列车进站端的半径为600 m的一曲线路段上随机出现多处严重轨头踏面掉块伤损。经对钢轨伤损状态的分析以及化学成分分析、拉伸性能测试和金相检验对掉块伤损的原因进行了分析。结果表明:钢轨轨头踏面的掉块伤损是由其表层的马氏体组织造成, 而马氏体组织的产生则是因列车车轮对钢轨的严重摩擦所引起的。
轨头踏面
掉块伤损
马氏体
摩擦
rail
rail head tread
peeling defects
martensite
friction
Abstract
A high-speed intercity railway was opened only about half a year, U71MnG 60 kg/m hot rolled rail was used in a station, the serious peeling defects were randomly appeared on the rail head tread of a line curve segment whose radius was 600 m at train terminal. By means of defect analysis, chemical composition analysis, tensile properties testing and metallographic examination, the reason of peeling defects was analyzed. The results showed that the peeling defects on rail head tread was caused by martensite on the surface layer, and martensite was due to serious friction between train wheels and rail.
中图分类号 U213.4+2
所属栏目 质量控制与失效分析
基金项目
收稿日期 2012/12/27
修改稿日期
网络出版日期
作者单位点击查看
备注邓勇(1977-),男,高级工程师。
引用该论文: DENG Yong,DENG Jian-hui. Reason Analysis on Defects in High-speed Railway Rail[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2013, 49(11): 766～769
邓勇,邓建辉. 某高速铁路钢轨伤损原因分析[J]. 理化检验－物理分册, 2013, 49(11): 766～769
被引情况:
【1】李闯,刘丰收,俞喆,梁旭,张银花,周清跃, "某高速铁路钢轨踏面伤损原因分析",理化检验－物理分册 51, 894-897(2015)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】邓建辉, 吴雄先, 孙明荣. U75V焊接钢轨线路铺设时的断裂原因分析[J].理化检验-物理分册, 2009, 45(10): 635-637.
【2】尤大勇.钢轨横截面出现斑痕的原因分析[J].理化检验-物理分册, 2003, 39(12):144-146.
【3】杨克, 卢观健.钢轨伤损图谱[M].北京: 中国铁道出版社, 1992.
【4】王栋.钢轨擦伤及其派生病害的分析与整治[J].山西科技, 2006(2): 113-114.
【5】张艳良.钢轨擦伤的调查分析及减缓措施[J].内蒙古煤炭经济, 2011(3): 91.
【2】尤大勇.钢轨横截面出现斑痕的原因分析[J].理化检验-物理分册, 2003, 39(12):144-146.
【3】杨克, 卢观健.钢轨伤损图谱[M].北京: 中国铁道出版社, 1992.
【4】王栋.钢轨擦伤及其派生病害的分析与整治[J].山西科技, 2006(2): 113-114.
【5】张艳良.钢轨擦伤的调查分析及减缓措施[J].内蒙古煤炭经济, 2011(3): 91.
相关信息