超声TOFD技术在小径厚壁管检测中的应用
Application of Ultrasonic TOFD Technique on Small Diameter Thick-Wall Pipe
摘 要
应用超声TOFD技术对规格为80 mm×19 mm的小径厚壁管进行了检测。阐述了TOFD探头楔块修磨后仪器相关参数的调整方法，并与相同厚度钢板进行了检测灵敏度对比。试验结果表明，TOFD探头楔块修磨至与被检管材相同曲率后，能够对焊缝内缺陷有效检出，且楔块修磨后检测灵敏度与相同厚度板材检测灵敏度相比，没有明显变化。
楔块
修磨
灵敏度
TOFD testing
Wedge
Wear
Sensitivity
Abstract
Abstract: Ultrasonic TOFD technique was used to detect the pipe for specification of 80 mm×19 mm. Regulation means of instrument parameters were explained for the wedge block after grinding and sensitivity comparison test was operated on the same thickness steel plate. The experimental result showed that the defect could be detected effectively after the wedge block being worn to the curvature as the pipe to be tested. Compared to the same thickness steel plate, no obvious change was observed for the test sensitivity.
中图分类号 TG115.28
所属栏目 试验研究
基金项目
收稿日期 2010/10/26
修改稿日期
网络出版日期
作者单位点击查看
备注齐向前(1978-)，男，工程师，硕士，从事无损检测技术及金属材料的研究。
引用该论文: QI Xiang-Qian. Application of Ultrasonic TOFD Technique on Small Diameter Thick-Wall Pipe[J]. Nondestructive Testing, 2011, 33(7): 29～31
齐向前. 超声TOFD技术在小径厚壁管检测中的应用[J]. 无损检测, 2011, 33(7): 29～31
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】李衍.ASME法规对超声TOFD法的最新规定介绍，第一部分：操作要领［J］.无损检测,2007,29(4):209-213.
【2】余国民,常永钢,丁小军,等.超声TOFD法在无损检测领域中的应用［J］.焊管,2007,30(6):39-44.
【3】韩相勇，姜自安,韩曙光,等.超声TOFD技术在管道环焊缝检测中的应用［J］.无损检测,2008,30(1):61-63.
【4】李海华，赵立凡,郭兴建,等.TOFD技术检测三维盲区的分析研究［J］.压力容器,2008,25(9):4-10.
【2】余国民,常永钢,丁小军,等.超声TOFD法在无损检测领域中的应用［J］.焊管,2007,30(6):39-44.
【3】韩相勇，姜自安,韩曙光,等.超声TOFD技术在管道环焊缝检测中的应用［J］.无损检测,2008,30(1):61-63.
【4】李海华，赵立凡,郭兴建,等.TOFD技术检测三维盲区的分析研究［J］.压力容器,2008,25(9):4-10.
相关信息