Test and Analysis of Delaminated Defect in TaW Thin-Plate
摘 要
针对1.6~3 mm厚度的TaW板线切割加工过程中产生的分层缺陷,研究了薄板分层缺陷的无损检测方法。结果表明,对薄板分层缺陷单独采用兰姆波检测容易造成漏检,而高频水浸超声检测方法能够灵敏地检测出薄板中的分层缺陷。结合加工工艺及金相分析手段,对TaW板加工过程中产生分层缺陷的原因进行了分析,结果表明,材质不佳以及线切割加工时产生的热应力是分层缺陷形成的原因。
Abstract
The effective non-destructive testing techniques were studied to test delaminated defect caused during line-cutting in thin-plate with thickness 1.6 to 3 mm. The results showed that the delaminated defect in thin plate might not be detected if only Lamb wave was used, but it was easy to detect delaminated defect with high frequency immersion ultrasonic. Combining the machining technology with the metallurgical analysis, the defect cause was analyzed. The results showed that poor quality material and hot stress from line-cutting were the main reasons causing delaminated defect.
中图分类号 TG115.28
所属栏目 试验研究
基金项目
收稿日期 2011/4/11
修改稿日期
网络出版日期
作者单位点击查看
备注李建文(1974-),男,硕士研究生,高级工程师,主要从事超声波无损检测技术研究。
引用该论文: LI Jian-Wen,WANG Zeng-Yong,MENG Yu-Tang. Test and Analysis of Delaminated Defect in TaW Thin-Plate[J]. Nondestructive Testing, 2012, 34(3): 32~34
李建文,王增勇,孟玉堂. TaW薄板分层缺陷检测及成因分析[J]. 无损检测, 2012, 34(3): 32~34
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】胡忠武,李中奎,张廷杰.钽及钽合金的新发展和应用[J].稀有金属与硬质合金,2003,31(3):34-36.
【2】彭海健,闫晓东,李德富.钽在破甲弹药型罩中的应用[J].稀有金属,2006,30(5):678-681.
【3】黄金昌.钽及其合金的性能和在化工中的应用[J].稀有金属快报,1995(3):1-3.
【4】王增勇,李建文,孙朝明.钽钨合金薄板的兰姆波检测[J].无损检测,2009,31(9):689-690.
【5】范同俐,廖玉龄.金属薄板中兰姆波的激励及分层的检查方法[J].无损检测,1982,4(6):6-10.
【6】郑开胜,刘景忠,白宝阳.薄板兰姆波探伤方法的评价[J].无损检测,1994,16(9):247-248.
【2】彭海健,闫晓东,李德富.钽在破甲弹药型罩中的应用[J].稀有金属,2006,30(5):678-681.
【3】黄金昌.钽及其合金的性能和在化工中的应用[J].稀有金属快报,1995(3):1-3.
【4】王增勇,李建文,孙朝明.钽钨合金薄板的兰姆波检测[J].无损检测,2009,31(9):689-690.
【5】范同俐,廖玉龄.金属薄板中兰姆波的激励及分层的检查方法[J].无损检测,1982,4(6):6-10.
【6】郑开胜,刘景忠,白宝阳.薄板兰姆波探伤方法的评价[J].无损检测,1994,16(9):247-248.
相关信息