奥氏体不锈钢中径管焊缝超声爬波探伤
Ultrasonic Creeping Wave Testing for the Welds of Middle-Bore Austenitic Stainless Steel Pipe
摘 要
为了有效解决传统超声波横波无法检测奥氏体不锈钢的问题，研制开发了超声爬波探头和对比试块。使用超声爬波技术对奥氏体中径管焊缝进行了全面检测，并对其性能进行验证。结果证明，采用超声爬波技术能有效检测出壁厚不大于18 mm的奥氏体中径管焊缝缺陷，可以作为奥氏体中径管焊缝的一种检测方法。
超声爬波
缺陷
无损检测
Middle-bore austenitic pipe weld
Ultrasonic creeping wave
Flaw
Nondestructive testing
Abstract
In order to effectively solve the problems faced by traditional shear wave testing on austenitic stainless steel，ultrasonic creeping wave probe and reference block were developed and fabricated. The creeping wave was used to perform a comprehensive testing of the welds of the middle-bore austenitic steel tubes and its effectiveness was verified. It is proved that the weld defects of the middle-bore austenitic steel tubes with wall thickness not more than 18mm can be detected by creeping wave inspection and the method can be used as a feasible method on austenitic weld.
中图分类号 TG115.28
所属栏目 试验研究
基金项目
收稿日期 2013/3/1
修改稿日期
网络出版日期
作者单位点击查看
备注王海军(1980-)，男，工程师，工学学士，主要从事电力工程安装、维修过程中金属理化检测和无损检测的技术工作。
引用该论文: WANG Hai-Jun,ZHAO You-Ming,JIN You-Dong,YIN Gao-Ming,CHEN Shi-Hua. Ultrasonic Creeping Wave Testing for the Welds of Middle-Bore Austenitic Stainless Steel Pipe[J]. Nondestructive Testing, 2013, 35(10): 22～24
王海军,赵有明,金友东,印高明,陈诗华. 奥氏体不锈钢中径管焊缝超声爬波探伤[J]. 无损检测, 2013, 35(10): 22～24
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】郑晖，林树青.《超声检测》.［M］.中国劳动社会保障出版社,2008:162-163.
【2】廉德良，魏天阳.超声爬波探头声场指向特性的试验研究.［J］.无损检测，2005，27(9)：479-481.
【3】王维东，韩玉峰，陆亚中等.小径管焊缝超声爬波探伤工艺方法研究.［J］无损探伤，2008，32(3)：36-41.
【2】廉德良，魏天阳.超声爬波探头声场指向特性的试验研究.［J］.无损检测，2005，27(9)：479-481.
【3】王维东，韩玉峰，陆亚中等.小径管焊缝超声爬波探伤工艺方法研究.［J］无损探伤，2008，32(3)：36-41.
相关信息