Failure Analysis on Fracture of an Engine Valve Spring
摘 要
采用宏微观分析、金相检验、显微硬度检测以及化学成分分析等方法对某汽车发动机气门弹簧的早期断裂原因进行了分析.结果表明:弹簧的断裂属性为疲劳断裂;弹簧钢丝原材料在淬火加热过程中与盐浴炉电极接触造成表面电弧烧伤形成麻坑,是引起该气门弹簧早期疲劳断裂的根本原因.
Abstract
Early fracture reasons of an automotive engine valve spring were investigated by means of macro and micro analysis,metallographic examination,micro hardness test and chemical compositions analysis.The results indicate that the failure property of the spring was fatigue fracture.The pockmark defect on the spring surface caused by electric arc burn during salt bath quenching heating was the root cause for the early fatigue fracture of the valve spring.
中图分类号 TG157 TG115
所属栏目 质量控制与失效分析
基金项目
收稿日期 2014/2/14
修改稿日期
网络出版日期
作者单位点击查看
备注王慧(1982-),男,工程师,博士.
引用该论文: WANG Hui,ZHU Ling-jing,WANG Ping,ZHANG An-qi,LIU Hai-bo,LING Ting. Failure Analysis on Fracture of an Engine Valve Spring[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2015, 51(2): 139~142
王慧,朱凌静,王平,张安琪,刘海波,凌婷. 发动机气门弹簧断裂失效分析[J]. 理化检验-物理分册, 2015, 51(2): 139~142
被引情况:
【1】王慧,廖为,孙国峰,刘海波, "自动扶梯扶手驱动轴断裂原因分析",理化检验-物理分册 52, 39-42(2016)
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】梁显斌.气门弹簧折断的危害[J].汽车维修,2006(7):11.
【2】孟凡西,闫行.55CrSi钢气门弹簧断裂原因分析[J].理化检验-物理分册,2009,45(7):446-447.
【3】程鹏,丁嘉怡,姜膺,等.过喷引起的气门弹簧断裂失效分析[J].金属热处理,2011,36(9):145-148.
【4】覃希治,刘丹平.盐浴加热淬火注意事项[J].金属加工:热加工,2013(3):43.
【5】肖玄,张航,杨林江,等.盐浴淬火高碳珠光体钢丝在冷拔过程中的显微组织及织构演变[J].机械工程材料,2013,37(10):39-43.
【6】杨辉,吴启梁.气门弹簧断裂的影响因素及原因分析[J].内燃机,2010(2):37-40.
【7】卢俊,万根节,张弛,等.国外气门弹簧线材实物质量分析[J].金属制品,2008,34(5):24-28.
【2】孟凡西,闫行.55CrSi钢气门弹簧断裂原因分析[J].理化检验-物理分册,2009,45(7):446-447.
【3】程鹏,丁嘉怡,姜膺,等.过喷引起的气门弹簧断裂失效分析[J].金属热处理,2011,36(9):145-148.
【4】覃希治,刘丹平.盐浴加热淬火注意事项[J].金属加工:热加工,2013(3):43.
【5】肖玄,张航,杨林江,等.盐浴淬火高碳珠光体钢丝在冷拔过程中的显微组织及织构演变[J].机械工程材料,2013,37(10):39-43.
【6】杨辉,吴启梁.气门弹簧断裂的影响因素及原因分析[J].内燃机,2010(2):37-40.
【7】卢俊,万根节,张弛,等.国外气门弹簧线材实物质量分析[J].金属制品,2008,34(5):24-28.
相关信息