Influence of Cold Working Deformation on Dislocation Density of IF steel
摘 要
研究了冷加工变形对IF钢位错密度的影响.结果表明:IF钢经冷加工变形后,晶体内产生大量位错,随着变形量逐渐增高,位错密度增大,位错开始相互缠结在一起,当变形量达到20%以上时,晶体内出现纤维组织,并进一步转变成胞状亚晶粒.在一定变形量范围内,平均位错密度ρ与变形量A符合线性关系:ρ=2.205 17×1014+1.049 5×1016A.
Abstract
The influence of cold working deformation on dislocation density of IF steel was studied.After the cold working deformation, there were amount of dislocations in IF steel.The dislocation density of IF steel increased with the increment of deformation extent.With the deformation up to 20%, the fibrous structure appeared in the crystal of IF steel, and became sub-grains.The relationship between dislocation density (ρ) and deformation amount (A) could be shown as the formula:ρ=2.205 17×1014+1.049 5×1016A.
中图分类号 TG3 O785+.7
所属栏目 试验与研究
基金项目
收稿日期 2014/11/12
修改稿日期
网络出版日期
作者单位点击查看
备注吉静(1985-),女,工程师,硕士.
引用该论文: JI Jing,WU Yi-wen,XU Ling-yun,WANG Biao,ZHU Zi-heng,WANG Hong-bin. Influence of Cold Working Deformation on Dislocation Density of IF steel[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2015, 51(3): 170~172
吉静,吴益文,徐凌云,王彪,朱子恒,汪宏斌. 冷加工变形对IF钢位错密度的影响[J]. 理化检验-物理分册, 2015, 51(3): 170~172
被引情况:
【1】徐凌云,吉静,黄菁,朱子恒,吴益文,汪宏斌, "固溶碳原子对IF钢Snoek内耗峰的影响",理化检验-物理分册 52, 156-158(2016)
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】李守华,李俊.汽车用高强度IF钢的研究进展[J].上海金属,2007,29(5):66-70.
【2】SATOH S.A new process for manufacturing deep-drawing cold-rolled steel sheet from ELC steels[J].Kawasaki Steel Technical Report, 1995(12):35-44.
【3】胡宽辉,田德新,冯冠文,等.汽车用热镀锌高强IF钢的研究进展[J].材料热处理技术,2010,39(18):34-38.
【4】张静江,王滨,奚建法,等.高锰低温钢晶体结构及位错形态研究[J].机械工程学报,1998,3(6):23-26.
【5】程万军,高占民,黄良驹.20CrMnTi钢的位错密度及晶体结构[J].吉林大学学报(工业版),2004,34(1):31-35.
【6】曹圣泉,张津徐,吴建生,等.IF钢再结晶晶粒尺寸、显微织构和晶界特征分布的EBSD研究[J].理化检验-物理分册,2004,40(4):163-167.
【7】王德宝,王越.高强IF钢板沿厚度方向的织构和显微组织[J].理化检验-物理分册,2010,46(6):348-351.
【8】HIRSCH P, HOWIE A, NICHOLSON R, et al.Electron Microscopy of Thin Crystals[M].Malabar, USA: Krieger Publishing Company,1997.
【9】LORETTO MH.Electron Beam Analysis of Materials[M].London: Chapman and Hall, 1994.
【10】PESICKA J, KUZEL R, DRONHOFER A, et al.The evolution of dislocation density during heat treatment and creep of tempered martensite ferritic steel[J].Acta Materialia, 2003(51):4847-4862.
【2】SATOH S.A new process for manufacturing deep-drawing cold-rolled steel sheet from ELC steels[J].Kawasaki Steel Technical Report, 1995(12):35-44.
【3】胡宽辉,田德新,冯冠文,等.汽车用热镀锌高强IF钢的研究进展[J].材料热处理技术,2010,39(18):34-38.
【4】张静江,王滨,奚建法,等.高锰低温钢晶体结构及位错形态研究[J].机械工程学报,1998,3(6):23-26.
【5】程万军,高占民,黄良驹.20CrMnTi钢的位错密度及晶体结构[J].吉林大学学报(工业版),2004,34(1):31-35.
【6】曹圣泉,张津徐,吴建生,等.IF钢再结晶晶粒尺寸、显微织构和晶界特征分布的EBSD研究[J].理化检验-物理分册,2004,40(4):163-167.
【7】王德宝,王越.高强IF钢板沿厚度方向的织构和显微组织[J].理化检验-物理分册,2010,46(6):348-351.
【8】HIRSCH P, HOWIE A, NICHOLSON R, et al.Electron Microscopy of Thin Crystals[M].Malabar, USA: Krieger Publishing Company,1997.
【9】LORETTO MH.Electron Beam Analysis of Materials[M].London: Chapman and Hall, 1994.
【10】PESICKA J, KUZEL R, DRONHOFER A, et al.The evolution of dislocation density during heat treatment and creep of tempered martensite ferritic steel[J].Acta Materialia, 2003(51):4847-4862.
相关信息