H62黄铜套管环境致裂行为分析
Environment Induced Cracking Behavior Analysis of H62 Copper Casings
摘 要
某批H62黄铜套管在装配时发生断裂,采用化学成分分析、宏观分析、光学显微镜和扫描电镜观察等方法对套管断裂原因进行了分析.结果表明:该H62黄铜套管断裂方式为沿晶断裂,是装配过程中的扭曲力、内部残余应力以及环境因素共同作用导致的应力腐蚀开裂.
套管
应力腐蚀开裂
环境致裂
H62 copper
casing
stress corrosion cracking
enviroment induced cracking
Abstract
Fracture failure happened to a batch of H62 copper casings when assembling,and means such as chemical compositions analysis,macro analysis,optical microscopy and scanning electron microscopy observation were used to analyze the fracture reasons of the casings.The results show that the fracture of the H62 copper casings with the characteristics of intergranular mode was stress corrosion cracking which was induced by the combined action of assembling twisting force,internal residual stress and environmental factors.
中图分类号 TG146.1+1 TG172.6
所属栏目 质量控制与失效分析
基金项目
收稿日期 2014/10/23
修改稿日期
网络出版日期
作者单位点击查看
备注杨晓(1985-),男,工程师,博士.
引用该论文: YANG Xiao,ZHANG Xian-feng,MIAO Fu-gui,LI Xue-feng. Environment Induced Cracking Behavior Analysis of H62 Copper Casings[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2015, 51(4): 283～285
杨晓,张先锋,苗富贵,李雪峰. H62黄铜套管环境致裂行为分析[J]. 理化检验－物理分册, 2015, 51(4): 283～285
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】吴平,王宜玲.H62黄铜管夹开裂分析[J].理化检验-物理分册,2003,39(3):162-164．
【2】孙智,江利,应鹏展.失效分析——基础与应用[M].北京:机械工业出版社,2005.
【3】徐国富,牟申周,李宏英,等.发电厂冷凝器黄铜管的断裂失效分析[J].湖北电力,2006,26(2):19-21．
【4】于利军,孙屏,于善伟.水表连接黄铜螺母断裂分析[J].理化检验-物理分册,2007,43(7):376-378．
【5】于淼.H62制紧固座开裂原因分析[J].失效分析与预防,2013,8(5):287-290．
【6】何叔麟.H62黄铜管的应力腐蚀破裂[J].腐蚀科学与防护技术,1992,4(3):212-214．
【7】顾美转.黄铜制品开裂原因分析[J].热加工工艺,2000(1):50-52．
【2】孙智,江利,应鹏展.失效分析——基础与应用[M].北京:机械工业出版社,2005.
【3】徐国富,牟申周,李宏英,等.发电厂冷凝器黄铜管的断裂失效分析[J].湖北电力,2006,26(2):19-21．
【4】于利军,孙屏,于善伟.水表连接黄铜螺母断裂分析[J].理化检验-物理分册,2007,43(7):376-378．
【5】于淼.H62制紧固座开裂原因分析[J].失效分析与预防,2013,8(5):287-290．
【6】何叔麟.H62黄铜管的应力腐蚀破裂[J].腐蚀科学与防护技术,1992,4(3):212-214．
【7】顾美转.黄铜制品开裂原因分析[J].热加工工艺,2000(1):50-52．
相关信息