热等静压处理后TC4钛合金中等轴α相特征及其对拉伸性能的影响
Characteristic of Equiaxed Alpha Phase in TC4 Titanium Alloy after Hot Isostatic Pressing and Effect of It on Tensile Properties
摘 要
对铸造TC4钛合金进行热等静压处理后,研究了TC4钛合金中等轴α相的特征及其对拉伸性能的影响,并对拉伸断口形貌进行了分析.结果表明:经热等静压处理后,在钛合金的三角晶界处可能会形成尺寸约为5 μm的等轴α相,因等轴α相含量较少,对拉伸性能的影响很小;含有等轴α相钛合金的拉伸断口上存在由大量韧窝组成的平台区.
铸造TC4钛合金
等轴α相
拉伸性能
断口
hot isostatic pressing
casted TC4 titanium alloy
equiaxed alpha phase
tensile property
fracture
Abstract
Hot isostatic pressing was carried on casted TC4 alloy,the characteristics of equiaxed alpha phase in TC4 titanium alloy and the effect of it on tensile properties were studied,and the tensile fracture also were analyzed.The results show that,after hot isostatic pressing,equiaxed alpha phase with size of 5 μm formed at triangle grain boundaries possibly,the small amounts of equiaxed alpha phase had little effect on the tensile properties.A platform area composed by amounts of dimples was founded on the tensile fracture of the alloy with equiaxed alpha phase.
中图分类号 TG335.81
所属栏目 试验研究
基金项目
收稿日期 2014/10/21
修改稿日期 2015/3/1
网络出版日期
作者单位点击查看
备注刘继雄(1983-),男,湖北孝感人,工程师,博士.
引用该论文: LIU Ji-xiong,YANG Qi,GUO Zhi-jun,WANG Ding-chun,GAO Qi,JIANG Hai-tao. Characteristic of Equiaxed Alpha Phase in TC4 Titanium Alloy after Hot Isostatic Pressing and Effect of It on Tensile Properties[J]. Materials for mechancial engineering, 2015, 39(5): 10～12
刘继雄,杨奇,郭志军,王鼎春,高颀,江海涛. 热等静压处理后TC4钛合金中等轴α相特征及其对拉伸性能的影响[J]. 机械工程材料, 2015, 39(5): 10～12
被引情况:
【1】李永林,曾卫东,陈林,沈立华,陈胜川,王璐,陈睿博, "热处理对Gr.38钛合金管组织和性能的影响",机械工程材料 40, 83-86(2016)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】胡桂珍,邬彦如.钛及钛合金的铸造[J].稀有金属材料与工程,1995,24(3):26-30.
【2】南海,谢成木,张润林.高强度模料的研制及在大型薄壁钛合金精铸件上的应用[J].机械工程材料,2002,26(3):15-16.
【3】JOVANOVIC′ M T,TADIC′ S,ZEC S,et al.The effect of annealing temperatures and cooling rates on microstructure and mechanical properties of investment cast Ti-6Al-4V alloy[J].Materials and Design,2006,27:192-199.
【4】王小娥,王红红.热等静压处理对ZT4钛合金精铸件组织与性能的影响[J].金属热处理,1992(4):30-34.
【5】陈迎旭,上官晓峰,马丽.铸造Ti-6Al-4V 合金拉伸断裂机理研究[J].铸造技术,2009,30(1):31-33.
【6】马丽,上官晓峰,要玉宏,等.铸造Ti-6Al-4V钛合金疲劳裂纹扩展特性的研究[J].铸造技术,2010,31(3):295-297.
【7】娄贯涛.热等静压和锻造对ZTC4组织及力学性能的影响[J].中国有色金属学报,2010,20(10):753-755.
【8】杨伟光,赵嘉琪,南海,等.热等静压工艺参量对ZTC4钛合金组织的影响规律[J].材料工程,2011(9):25-28.
【9】杨伟光,赵嘉琪,南海,等.热等静压工艺参数对ZTC4钛合金力学性能的影响[J].材料工程,2011(10):42-46.
【10】钱学梅,钱学军,吕彦,等.静液挤压变形工艺对TC4钛合金组织与性能的影响[J].兵器材料科学与工程,2011,34(4):77-79.
【2】南海,谢成木,张润林.高强度模料的研制及在大型薄壁钛合金精铸件上的应用[J].机械工程材料,2002,26(3):15-16.
【3】JOVANOVIC′ M T,TADIC′ S,ZEC S,et al.The effect of annealing temperatures and cooling rates on microstructure and mechanical properties of investment cast Ti-6Al-4V alloy[J].Materials and Design,2006,27:192-199.
【4】王小娥,王红红.热等静压处理对ZT4钛合金精铸件组织与性能的影响[J].金属热处理,1992(4):30-34.
【5】陈迎旭,上官晓峰,马丽.铸造Ti-6Al-4V 合金拉伸断裂机理研究[J].铸造技术,2009,30(1):31-33.
【6】马丽,上官晓峰,要玉宏,等.铸造Ti-6Al-4V钛合金疲劳裂纹扩展特性的研究[J].铸造技术,2010,31(3):295-297.
【7】娄贯涛.热等静压和锻造对ZTC4组织及力学性能的影响[J].中国有色金属学报,2010,20(10):753-755.
【8】杨伟光,赵嘉琪,南海,等.热等静压工艺参量对ZTC4钛合金组织的影响规律[J].材料工程,2011(9):25-28.
【9】杨伟光,赵嘉琪,南海,等.热等静压工艺参数对ZTC4钛合金力学性能的影响[J].材料工程,2011(10):42-46.
【10】钱学梅,钱学军,吕彦,等.静液挤压变形工艺对TC4钛合金组织与性能的影响[J].兵器材料科学与工程,2011,34(4):77-79.
相关信息