超超临界汽轮机IN783螺栓断裂原因分析
Analysis on Fracture Reason of IN783 Bolt Applied in Ultra Supercritical Steam Turbine
摘 要
某电厂汽轮机运行过程中在其中调门IN783合金螺栓的光杆处发生断裂.通过宏观和微观观察、化学成分和性能检测的基础上,对螺栓断裂的原因进行了分析.结果表明：螺栓断裂起源于中心孔壁,断口以沿晶脆性形貌为主,断裂性质为应力加速晶界氧化(SAGBO)脆性断裂;β时效处理不合格导致SAGBO抗力不足是螺栓发生断裂的主要原因.
螺栓
脆性断裂
β时效处理
应力加速晶界氧化
alloy IN783
bolt
brittle fracture
aging of β phases
SAGBO
Abstract
A pressure regulator valve bolt made by alloy IN783 in a power plant was fractured at the position of bolt waist during operation.Based on macro and micro observation, chemical composition and mechanical property inspection, the fracture reason of bolt was investigated.The results showed that fracture originated from the center hole wall, the main characteristic of fracture was intergranular brittleness morphology, and the fracture mode was brittle fracture caused by stress accelerated grain boundary oxidative (SAGBO);the lower resistance of SAGBO due to aging treatment failure of β phases was the main case of fracture.
中图分类号 TH131.3
所属栏目 质量控制与失效分析
基金项目
收稿日期 2014/7/22
修改稿日期
网络出版日期
作者单位点击查看
备注杨超(1979-),男,高级工程师,学士.
引用该论文: YANG Chao,FENG Li-zhong,WU Hong-tao,YANG Xian-biao. Analysis on Fracture Reason of IN783 Bolt Applied in Ultra Supercritical Steam Turbine[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2015, 51(5): 346～349
杨超,冯立中,吴红涛,杨贤彪. 超超临界汽轮机IN783螺栓断裂原因分析[J]. 理化检验－物理分册, 2015, 51(5): 346～349
被引情况:
【1】王家庆, "某600 MW燃煤发电机组调门螺栓理化性能检验",理化检验－物理分册 52, 257-259(2016)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】Tundermann J H.Development of IN783 alloy, a low thermal expention, crack growth resistant superalloy[J].Acta Metallurgica Sinica,1996,12:503-507.
【2】张艳艳,韩光炜,邓波,等.IN783合金的相组成和组织结构[J].钢铁研究学报,2007,19(4):58-61.
【3】张立新,孙奇.K444铸造高温合金的高温蠕变性能[J].理化检验-物理分册,2013,49(8):510-515.
【4】沈治.INCONEL783合金的组织与应力弛豫性能研究[D].上海:上海交通大学,2010.
【5】段辉,甑小辉,吴锐红.热处理对IN783合金组织和拉伸性能的影响[J].热加工工艺,2012,41(2):205-207.
【6】郭景锋,徐仁根.Fe-25Cr-35Ni系合金中的第二相[J].理化检验-物理分册,2012,48(8):500-503.
【2】张艳艳,韩光炜,邓波,等.IN783合金的相组成和组织结构[J].钢铁研究学报,2007,19(4):58-61.
【3】张立新,孙奇.K444铸造高温合金的高温蠕变性能[J].理化检验-物理分册,2013,49(8):510-515.
【4】沈治.INCONEL783合金的组织与应力弛豫性能研究[D].上海:上海交通大学,2010.
【5】段辉,甑小辉,吴锐红.热处理对IN783合金组织和拉伸性能的影响[J].热加工工艺,2012,41(2):205-207.
【6】郭景锋,徐仁根.Fe-25Cr-35Ni系合金中的第二相[J].理化检验-物理分册,2012,48(8):500-503.
相关信息