某超临界机组锅炉过热器管爆管原因分析
Analysis on Bursting Reason of Super-heater Tubes of a Supercritical Boiler
摘 要
通过化学成分分析、力学性能测试、宏观和微观检验等手段对某电厂末级过热器T91钢管爆裂的原因进行了分析.结果表明：爆管具有短时超温运行的特征,爆口附近发生明显的塑性变形,材料显微组织老化严重,力学性能显著下降.导致爆管超温运行的原因可能是两异径管接头处焊瘤和管内壁剥落的氧化皮在下弯头处堆积造成高温蒸汽堵塞,从而引起管壁局部短时超温.
过热器
T91钢管
爆管
超温运行
氧化皮
boiler
super-heater
T91 steel tube
burst tube
overheat operation
oxide skin
Abstract
The bursting reason of a final super-heater T91 steel tube in a power plant was analyzed through chemical composition analysis, mechanical property testing, macro and micro examination.The results showed that, the burst tube had characteristics of overheat operation for short term, obvious plastic deformation was happened, the microstructure of the material aged seriously, and the mechanical properties decreased significantly near the burst mouth.The reason of overheat operation in the burst tube was possibly that, high temperature steam was blocked by weld beadings of the joint between two different diameter tubes and oxide skin spalling from the tube wall accumulated at the elbow tube, thus overheat operation for short term was caused in the tube local wall.
中图分类号 TM621.2
所属栏目 质量控制与失效分析
基金项目
收稿日期 2014/6/4
修改稿日期
网络出版日期
作者单位点击查看
备注蒙新明(1980-),男,工程师,硕士.
引用该论文: MENG Xin-ming,ZHANG Lu,LAI Yun-ting,YU Min,ZHANG Guo-dong. Analysis on Bursting Reason of Super-heater Tubes of a Supercritical Boiler[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2015, 51(5): 353～357
蒙新明,张路,赖云亭,於旻,张国栋. 某超临界机组锅炉过热器管爆管原因分析[J]. 理化检验－物理分册, 2015, 51(5): 353～357
被引情况:
【1】刘燕,汤杰,苏成功,王威强, "连续球压痕法测试钢管应变时效后拉伸强度的变化",理化检验－物理分册 52, 77-82(2016)
【2】卢书媛,王卫忠,俞璐,徐海斌,朱一波, "锅炉过热器管爆裂原因分析",理化检验－物理分册 52, 807-810(2016)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】肖国华,李益民,王理博.超超临界机组锅炉末级过热器爆管原因分析[J].理化检验-物理分册,2011,47(4):245-247.
【2】赵彦芬,张路,王正品,等.高温过热器T91,T22管爆管分析[J].热力发电,2004,11:61-64.
【3】包文东,郑坊评,崔雄华,等.超临界锅炉末级过热器T91钢管爆管原因分析及预防措施[J].理化检验-物理分册,2012,48(10):704-707.
【4】束国刚,刘江南,石崇哲,等.超临界锅炉用T/P91钢的组织性能与工程应用[M].西安:陕西科学技术出版社,2006:256-258.
【5】王正品,张路,刘江南,等.电站用T22及与T91管高温蒸汽氧化的失效分析[J].铸造技术,2004,25(7):523-525.
【6】李鹏辉,刘宗茂,周庞.关于T91钢寿命评估方法的探讨[J].河北工业科技,2007,24(5):255-258.
【7】张路,赵彦芬,刘艳,等.高温受热面管材质抗氧化温度对锅炉材料设计选型、运行的影响[J].中国电机工程学报,2012,32(增刊1):384-390.
【8】赵彦芬,张路,刘艳,等.超超临界机组T92钢高温受热面管爆管原因分析[J].理化检验-物理分册,2012,48(3):180-184.
【9】李续军,苗迺金,高景辉.关于600 MW级超临界机组蒸汽参数的选择分析[J].热力透平,2003(1):58-62.
【10】祝毅,杨宁,徐耀良,等.600 MW超临界锅炉过热器爆管原因及改进措施[J].华东电力,2011,39(8):1340-1342.
【2】赵彦芬,张路,王正品,等.高温过热器T91,T22管爆管分析[J].热力发电,2004,11:61-64.
【3】包文东,郑坊评,崔雄华,等.超临界锅炉末级过热器T91钢管爆管原因分析及预防措施[J].理化检验-物理分册,2012,48(10):704-707.
【4】束国刚,刘江南,石崇哲,等.超临界锅炉用T/P91钢的组织性能与工程应用[M].西安:陕西科学技术出版社,2006:256-258.
【5】王正品,张路,刘江南,等.电站用T22及与T91管高温蒸汽氧化的失效分析[J].铸造技术,2004,25(7):523-525.
【6】李鹏辉,刘宗茂,周庞.关于T91钢寿命评估方法的探讨[J].河北工业科技,2007,24(5):255-258.
【7】张路,赵彦芬,刘艳,等.高温受热面管材质抗氧化温度对锅炉材料设计选型、运行的影响[J].中国电机工程学报,2012,32(增刊1):384-390.
【8】赵彦芬,张路,刘艳,等.超超临界机组T92钢高温受热面管爆管原因分析[J].理化检验-物理分册,2012,48(3):180-184.
【9】李续军,苗迺金,高景辉.关于600 MW级超临界机组蒸汽参数的选择分析[J].热力透平,2003(1):58-62.
【10】祝毅,杨宁,徐耀良,等.600 MW超临界锅炉过热器爆管原因及改进措施[J].华东电力,2011,39(8):1340-1342.
相关信息