法兰套管件调质处理开裂原因分析
Analysis on Cracking Reason of Flange Sleeve Parts after Quenching and Tempering
摘 要
某输油管道用法兰套管件,在热加工锻造、调质处理后法兰边缘出现周向开裂.通过化学成分分析和金相检验对法兰套管件开裂的原因进行了分析.结果表明：工件在锻造加工过程中,加热温度过高,加热时间过长,工件过热过烧,形成晶间氧化,晶间结合力显著降低,组织脆化,导致热加工锻造开裂.
过热
过烧
晶间氧化
锻造开裂
flange sleeve
overheating
overburning
intergranular oxidation
forging cracking
Abstract
The circumferential cracking was found on the edge of flange sleeve parts for oil pipeline after the hot forging,quenching and tempering.Through chemical composition analysis and metallographic examination,the cracking reason of flange sleeve parts was analyzed.The results showed that the intergranular oxidation was formed in flange sleeve parts,which was overheating or overburning in the forging process,because the heating temperature was too high and the heating time was too long.The intergranular binding capacity decreased significantly,the microstructure was embrittled,led to hot forging cracking in the parts.
中图分类号 TE973 DOI 10.11973/lhjy-wl201507015
所属栏目 质量控制与失效分析
基金项目
收稿日期 2014/4/9
修改稿日期
网络出版日期
作者单位点击查看
备注金林奎(1966-),男,质量工程师,热处理高级技师,材料热处理工程师,学士.
引用该论文: JIN Lin-kui,ZHAO Jian-guo,WANG Chun-liang. Analysis on Cracking Reason of Flange Sleeve Parts after Quenching and Tempering[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2015, 51(7): 504～507
金林奎,赵建国,王春亮. 法兰套管件调质处理开裂原因分析[J]. 理化检验－物理分册, 2015, 51(7): 504～507
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】马鹏飞,李美兰,戈晓岚.热处理技术[M].北京:化学工业出版社,2008:85-87.
【2】吕炎,王尔德,钱存济,等.锻件组织性能控制[M].北京:国防工业出版社,1988:218-220.
【3】张学彬,缪振华,蒋月娟,等.40Cr钢机油泵轴断裂分析[J].理化检验-物理分册,2010,46(4):257-258.
【4】樊东黎,徐跃明,董晓辉.热处理工程师手册[M].北京:机械工业出版社,2004:23-25.
【5】郑学坊,邱允新,唐镇南.金相分析技术[M].上海:上海科学技术文献出版社,1987:198-199.
【6】张菊水,赵坚,黄存瑛,等.钢的过热过烧[M].上海:上海科学技术出版社,1984:26-29.
【7】谭国良,杨浩义,杨冬梅.轮胎螺栓断裂失效分析[J].理化检验-物理分册,2006,42(11):577-579.
【2】吕炎,王尔德,钱存济,等.锻件组织性能控制[M].北京:国防工业出版社,1988:218-220.
【3】张学彬,缪振华,蒋月娟,等.40Cr钢机油泵轴断裂分析[J].理化检验-物理分册,2010,46(4):257-258.
【4】樊东黎,徐跃明,董晓辉.热处理工程师手册[M].北京:机械工业出版社,2004:23-25.
【5】郑学坊,邱允新,唐镇南.金相分析技术[M].上海:上海科学技术文献出版社,1987:198-199.
【6】张菊水,赵坚,黄存瑛,等.钢的过热过烧[M].上海:上海科学技术出版社,1984:26-29.
【7】谭国良,杨浩义,杨冬梅.轮胎螺栓断裂失效分析[J].理化检验-物理分册,2006,42(11):577-579.
相关信息