DEVELOPMENT OF CORROSION INHIBITORS FOR REINFORCING STEEL
摘 要
混凝土中钢筋的腐蚀是钢筋混凝土建筑过早损坏的主要原因.氯离子的进入是加速此种腐蚀的关键因素.文章着重介绍阻止钢筋混凝土腐蚀的阻锈剂的发展及迁移型阻锈剂的行为特点.阻锈剂技术的发展趋势和今后的研究工作需要进一步的探究.
Abstract
Corrosion of reinforcing rebar is the main reason of premature failure of reinforced concrete structures.The ingress of chloride is the key phenomenon promoting such corrosion.This paper introduces the development of corrosion inhibitors to prevent corrosion of reinforcement concrete,action performance of migrating corrosion inhibitors,trend of corrosion inhibitor technology and future research work.
中图分类号 TG174.4 TU503
所属栏目 综述
基金项目 上海市重点培育学科(P1304)和国家自然科学基金资助课题(20576069)
收稿日期 2005/10/10
修改稿日期 2005/12/20
网络出版日期
作者单位点击查看
引用该论文: WANG Wei,ZHANG Da-quan,ZHANG Wan-you,ZHOU Guo-ding. DEVELOPMENT OF CORROSION INHIBITORS FOR REINFORCING STEEL[J]. Corrosion & Protection, 2006, 27(7): 369~373
被引情况:
【1】沈忠,王青海,陈洁,何艺峰,张永浩,刘艳,刘莉, "几种缓蚀剂对膨润土中16MnR钢的缓蚀作用",腐蚀与防护 33, 585-588(2012)
【2】耿春雷, "低掺量钢筋阻锈剂的性能及机理",腐蚀与防护 32, 908-912(2011)
【3】刘艳,王青海,赵维霞,张永浩,刘勇,刘伟, "16MnR钢在多种回填材料中的腐蚀行为",腐蚀与防护 31, 440-443(2010)
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】洪定海.钢筋腐蚀引起混凝土结构破坏的修复对策[J].建筑材料学报,1998,1(3):271-277.
【2】李伟.钢筋阻锈剂的防腐机理及相关规范[J].有色矿山,2000,29(4):49-50.
【3】洪乃丰.钢筋阻锈剂的发展与应用[J].工业建筑,2005,35(6):68-70.
【4】Montemor M F,Simoes A M P,Ferreira M G S.Chloride-induced orrosion on reinforcing steel:from the fundamentals to the monitoring techniques[J].Cement & Concrete Composites,2003,25:491-502.
【5】Glass G K,Buenfeld N R.The presentation of the chloride threshold level for corrosion of steel in concrete[J].Corrosion Science,1997,39(5):1001-1013.
【6】Mammoliti L,Hansson C M,Hope B B.Corrosion inhibitors in concrete Part II:Effect on chloride threshold values for corrosion of steel in synthetic pore solutions[J].Cement and Concrete Research,1999,29:1583-1589.
【7】Omar S.Baghabra Al-Amoudi,Mohammed Maslehudin,et al.Effectiveness of corrosion inhibitors in contaminated concrete[J].Cement & Concrete Composites,2003,25:439-449.
【8】张小冬,周 庆,陈 烈.钢筋阻锈剂的应用发展概况[J].施工技术,2004,33(6):52-53.
【9】Ngala V T,Page C L,Page M M.Corrosion inhibitor systems for remedial treatment of reinforced concrete.Part 1:calcium nitrite[J].Corro Sci,2002,44:2073-2087.
【10】Hansson C M,Mammoliti L,Hope B B.Corrosion inhibitors in concrete-part Ⅰ:the principles[J].Cement and Concrete Research,1998,28(12):1775-1781.
【11】Alonso C,Andrade C,Argiz C,et al.Na2PO3F as inhibitor of corroding reinforcement in carbonated concrete[J].Cement and Concrete Research,1996,26(3):405-415.
【12】Ngala V T,Page C L,Page M M.Corrosion inhibitor systems for remedial treatment of reinforced concrete.Part 2:sodium monofluorophosphate[J].Corro Sci,2003,45:1523-1537.
【13】Monticelli C,Frignani A,Trabanelli G.A study on corrosion inhibitors for concrete application [J].Cement and Concrete Research,2000,30:635-642.
【14】徐永膜.迁移性阻锈剂——钢筋混凝土阻锈剂的新发展[J].硅酸盐学报,2002,30(1):94-100.
【15】Morris W,Vico A,Vazquez M.Corrosion of reinforcing steel by means of concrete resistivity measurements[J].Corrosion Science,2002,44:81-99.
【16】Tritthart J.Transport of a surface-applied corrosion inhibitor in cement paste and concrete [J].Cement and Concrete Research,2003,33:829-834.
【17】张大全,安仲勋,潘庆谊,等.吗啉多元胺对混凝土钢筋的阻锈作用[J].材料保护,2004,37(8):4-6.
【18】马新伟,邝静哲,范征玉.钢筋阻锈剂的新发展[J].等温建筑技术,2004,6:7-8.
【19】王胜先,林薇薇,张鉴清,等.硫脲-二乙烯三胺缩聚物对混凝土中钢筋的缓蚀作用[J].中国腐蚀与防护学报,2000,20(1):15-20.
【20】Zhang Da-quan,Gao Li-xin,Zhou Guo-ding.Synergistic effect of 2-Mercapto benzimidazole and KI on copper corrosion inhibition in aerated sulfuric acid solution [J].Journal of Applied Electrochemistry,2003,33(5):361-366.
【21】Saraswathy V,Muralidharan S,Kalyanasundaram R M,et al.Evaluation of a composite corrosion-inhibiting admixture and its performance in concrete under macrocell corrosion conditions[J].Cement and Concrete Research,2001,31:789-794.
【22】Rincon O,Perez O,Paredes E.Long-term performance of ZnO as a rebar corrosion inhibitor[J].Cement & Concrete Composites,2002,24:79-87.
【23】Batis G,Pantazopoulou P,Routoulas A.Corrosion protection investigation of reinforcement by inorganic coating in the presence of alkanolamine-based inhibitor[J].Cement & Concrete Composites,2003,25:371-377.
【24】Dhouibi L,Triki E,Raharinaivo A.The application of electrochemical impedance spectroscopy to determine the long-term effectiveness of corrosion inhibitors for steel in concrete[J].Cement & Concrete Composites,2002,24:35-43.
【25】Hu R G,Lin C J,Zhao B,et al.Acompreahansive study on the corrosion behavior for reinforced steel in concrete[A].16th International Corrosion Congress,Paper08-18[C].China(Beijing):2005.
【2】李伟.钢筋阻锈剂的防腐机理及相关规范[J].有色矿山,2000,29(4):49-50.
【3】洪乃丰.钢筋阻锈剂的发展与应用[J].工业建筑,2005,35(6):68-70.
【4】Montemor M F,Simoes A M P,Ferreira M G S.Chloride-induced orrosion on reinforcing steel:from the fundamentals to the monitoring techniques[J].Cement & Concrete Composites,2003,25:491-502.
【5】Glass G K,Buenfeld N R.The presentation of the chloride threshold level for corrosion of steel in concrete[J].Corrosion Science,1997,39(5):1001-1013.
【6】Mammoliti L,Hansson C M,Hope B B.Corrosion inhibitors in concrete Part II:Effect on chloride threshold values for corrosion of steel in synthetic pore solutions[J].Cement and Concrete Research,1999,29:1583-1589.
【7】Omar S.Baghabra Al-Amoudi,Mohammed Maslehudin,et al.Effectiveness of corrosion inhibitors in contaminated concrete[J].Cement & Concrete Composites,2003,25:439-449.
【8】张小冬,周 庆,陈 烈.钢筋阻锈剂的应用发展概况[J].施工技术,2004,33(6):52-53.
【9】Ngala V T,Page C L,Page M M.Corrosion inhibitor systems for remedial treatment of reinforced concrete.Part 1:calcium nitrite[J].Corro Sci,2002,44:2073-2087.
【10】Hansson C M,Mammoliti L,Hope B B.Corrosion inhibitors in concrete-part Ⅰ:the principles[J].Cement and Concrete Research,1998,28(12):1775-1781.
【11】Alonso C,Andrade C,Argiz C,et al.Na2PO3F as inhibitor of corroding reinforcement in carbonated concrete[J].Cement and Concrete Research,1996,26(3):405-415.
【12】Ngala V T,Page C L,Page M M.Corrosion inhibitor systems for remedial treatment of reinforced concrete.Part 2:sodium monofluorophosphate[J].Corro Sci,2003,45:1523-1537.
【13】Monticelli C,Frignani A,Trabanelli G.A study on corrosion inhibitors for concrete application [J].Cement and Concrete Research,2000,30:635-642.
【14】徐永膜.迁移性阻锈剂——钢筋混凝土阻锈剂的新发展[J].硅酸盐学报,2002,30(1):94-100.
【15】Morris W,Vico A,Vazquez M.Corrosion of reinforcing steel by means of concrete resistivity measurements[J].Corrosion Science,2002,44:81-99.
【16】Tritthart J.Transport of a surface-applied corrosion inhibitor in cement paste and concrete [J].Cement and Concrete Research,2003,33:829-834.
【17】张大全,安仲勋,潘庆谊,等.吗啉多元胺对混凝土钢筋的阻锈作用[J].材料保护,2004,37(8):4-6.
【18】马新伟,邝静哲,范征玉.钢筋阻锈剂的新发展[J].等温建筑技术,2004,6:7-8.
【19】王胜先,林薇薇,张鉴清,等.硫脲-二乙烯三胺缩聚物对混凝土中钢筋的缓蚀作用[J].中国腐蚀与防护学报,2000,20(1):15-20.
【20】Zhang Da-quan,Gao Li-xin,Zhou Guo-ding.Synergistic effect of 2-Mercapto benzimidazole and KI on copper corrosion inhibition in aerated sulfuric acid solution [J].Journal of Applied Electrochemistry,2003,33(5):361-366.
【21】Saraswathy V,Muralidharan S,Kalyanasundaram R M,et al.Evaluation of a composite corrosion-inhibiting admixture and its performance in concrete under macrocell corrosion conditions[J].Cement and Concrete Research,2001,31:789-794.
【22】Rincon O,Perez O,Paredes E.Long-term performance of ZnO as a rebar corrosion inhibitor[J].Cement & Concrete Composites,2002,24:79-87.
【23】Batis G,Pantazopoulou P,Routoulas A.Corrosion protection investigation of reinforcement by inorganic coating in the presence of alkanolamine-based inhibitor[J].Cement & Concrete Composites,2003,25:371-377.
【24】Dhouibi L,Triki E,Raharinaivo A.The application of electrochemical impedance spectroscopy to determine the long-term effectiveness of corrosion inhibitors for steel in concrete[J].Cement & Concrete Composites,2002,24:35-43.
【25】Hu R G,Lin C J,Zhao B,et al.Acompreahansive study on the corrosion behavior for reinforced steel in concrete[A].16th International Corrosion Congress,Paper08-18[C].China(Beijing):2005.
相关信息