高纯锌参比电极电位稳定性研究
POTENTIAL STABILITY OF 99.9999% HIGH PURITY ZINC REFERENCE ELECTRODE
摘 要
采用电化学方法研究了氯离子浓度、温度、阳极极化电流及三者间相互协同作用对99.9999%高纯锌参比电极电位稳定性的影响.结果表明,常温(25℃)下氯离子浓度越高,电极的稳定电位越负；在海水中,偏离25℃,温度升高或降低时,电极电位都会负移,当温度达到50℃时,锌上沉积的腐蚀产物结构改变使锌的电极电位正移；海水温度在0-25℃,阳极极化电流＜5μA/cm2,高纯锌具有良好的电流负载能力.
氯离子浓度
温度
阳极极化电流
High purity zinc
Cl- concentration
Temperature
Anodic polarization current
Abstract
The effect of Cl- concentration,temperature and anodic polarization current on the potential stability of high purity zinc reference electrode was investigated.The higher the Cl- concentration,the more negative the electrode potential.The potential shifted to the negative value while the temperature was higher or lower than 25℃,but it shifted to positive at 50℃ due to the deposition of corrosion product on the electrode surface.When the seawater temperature was between 0℃ and 25℃,and the anodic polarization current was lower than 5μA/cm2,high purity zinc exhibited high performance of current-load ability.
中图分类号 TG174.41
所属栏目 试验研究
基金项目
收稿日期 2005/11/1
修改稿日期 2005/12/1
网络出版日期
作者单位点击查看
引用该论文: WANG Zeng-di,YAN Yong-gui,MA Li,QIAN Jian-hua,CHEN Guang-zhang,LI Qing-fen. POTENTIAL STABILITY OF 99.9999% HIGH PURITY ZINC REFERENCE ELECTRODE[J]. Corrosion & Protection, 2006, 27(9): 450～453
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】曹楚南.腐蚀电化学原理[M].北京:化学工业出版社,2004.14.
【2】胡士信.阴极保护工程手册[M].北京:化学工业出版社,1999.142.
【3】彭乔,殷正安,郭建伟.高纯锌参比电极电化学行为研究[J].全面腐蚀控制,1993,(5):22-25.
【4】陈国华,王光信.电化学方法应用[M].北京:化学工业出版社,2003.245.
【5】国家标准GB/T 7387-1999 船用参比电极技术条件[S].
【2】胡士信.阴极保护工程手册[M].北京:化学工业出版社,1999.142.
【3】彭乔,殷正安,郭建伟.高纯锌参比电极电化学行为研究[J].全面腐蚀控制,1993,(5):22-25.
【4】陈国华,王光信.电化学方法应用[M].北京:化学工业出版社,2003.245.
【5】国家标准GB/T 7387-1999 船用参比电极技术条件[S].
相关信息