EFFECT OF NITROGEN ON DAMPING AND CORROSIVE PROPERTIES OF Fe-Mn ALLOYS
摘 要
通过内耗检测技术研究了氮对Fe-14.1Mn和Fe-16.5Mn合金阻尼性能及对Fe-Mn系合金相组成和抗腐蚀性能的影响.结果表明:Fe-14.1Mn比Fe-16.5Mn合金具有更高的阻尼性能;合金中加入质量分数为0.2%的氮,两种合金的阻尼性能略有改变,合金在固溶处理时,发生了γ-ε转变,转变生成的马氏体越多,合金的阻尼性能越好;并且含氮合金在1mol/L硫酸水溶液中的抗腐蚀性能提高2倍.
Abstract
The influence of nitrogen on the damping capacity of Fe-14.1Mn and Fe-16.5Mn alloys was studied using amplitude-dependent internal friction technique.The effect of nitrogen on phase constitution,mechanical properties and corrosion resistance was investigated.The Fe-14.1Mn alloy possessed a much higher level of damping capacity than the Fe-16.5Mn alloy.The addition of approximately 0.2 wt.% of nitrogen slightly affected the damping capacity of the Fe-14.1Mn alloy and increased the damping capacity in the Fe-16.5Mn alloy.The more austenite converted to martensite,the better damping capacity was obtained after heat treatment.The corrosion resistance of both alloys in 1mol/L sulphuric acid solution was improved by more than two times due to nitrogen alloying.
中图分类号 TG135+.7 TG174.2
所属栏目 试验研究
基金项目
收稿日期 2006/3/8
修改稿日期 2006/5/18
网络出版日期
作者单位点击查看
引用该论文: YU Xue-yong,HUA Zheng-xiao,CHENG feng-jun,LI-Ning,DONG Shou-jun. EFFECT OF NITROGEN ON DAMPING AND CORROSIVE PROPERTIES OF Fe-Mn ALLOYS[J]. Corrosion & Protection, 2006, 27(12): 614~616
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】Joong Hwan Jun,S H Baik,Young Kook Lee,et al.The influence of aging on damping capacity of Fe-17Mn-X%C alloy[J].Scripta Materialia,1998,39(1):34-39.
【2】Joong Hwan Jun,Chong Sool Choi.The influence of Mn content on microstructure and damping capacity in Fe-(17-23)%Mn alloys[J].Materials Science and Engineering,1998,A252(2):133-138.
【3】Young Kook Lee,Joong Hwan Jun,Chong Sool Choi.Effect of εmartensite content on the damping capacity of Fe-Mn alloy[J].Scripta Materialia,1996,35(7):825-830.
【4】于学勇,李 宁,等.预变形量对Fe-14Mn-0.22C合金阻尼性能的影响[J].金属热处理,2004,29(10):24-26.
【5】Young Kook Lee,Joong Hwan Jun,Chong Sool Choi.Damping mechanisms of Fe-Mn alloy with (γ+ε) dual phase structure[J].Materials Science and Technoloy,2000,16(4):389-390.
【6】李 宁,胥永刚,于学勇.热处理对Fe-14Mn-0.2C合金阻尼性能的影响[J].机械工程材料,2004,28(11):7-9.
【2】Joong Hwan Jun,Chong Sool Choi.The influence of Mn content on microstructure and damping capacity in Fe-(17-23)%Mn alloys[J].Materials Science and Engineering,1998,A252(2):133-138.
【3】Young Kook Lee,Joong Hwan Jun,Chong Sool Choi.Effect of εmartensite content on the damping capacity of Fe-Mn alloy[J].Scripta Materialia,1996,35(7):825-830.
【4】于学勇,李 宁,等.预变形量对Fe-14Mn-0.22C合金阻尼性能的影响[J].金属热处理,2004,29(10):24-26.
【5】Young Kook Lee,Joong Hwan Jun,Chong Sool Choi.Damping mechanisms of Fe-Mn alloy with (γ+ε) dual phase structure[J].Materials Science and Technoloy,2000,16(4):389-390.
【6】李 宁,胥永刚,于学勇.热处理对Fe-14Mn-0.2C合金阻尼性能的影响[J].机械工程材料,2004,28(11):7-9.
相关信息