马氏体沉淀硬化不锈钢0Cr13Ni8Mo2Al的腐蚀性能
CORROSION PROPERTIES OF 0Cr13Ni8Mo2Al STAINLESS STEEL
摘 要
研究了马氏体沉淀硬化不锈钢0Cr13Ni8Mo2Al的腐蚀性能,即应力腐蚀敏感性、抗氧化性能和抗盐雾腐蚀性能等.研究表明该钢具有较好的抗应力腐蚀性能,其应力腐蚀断裂形貌为穿晶、解理断裂,并有二次裂纹.500℃抗氧化性能很好,属于完全抗氧化级.抗盐雾腐蚀性能较好,经500h盐雾腐蚀试验,试样表面只有轻微的锈蚀,腐蚀速率较低.
应力腐蚀破裂
抗氧化
盐雾腐蚀
0Cr13Ni8Mo2Al stainless steel
SCC
Anti-oxidization
Salt spray corrosion
Abstract
The corrosion properties including stress corrosion cracking (SCC),anti-oxidization and salt spray corrosion of 0Cr13Ni8Mo2Al stainless steel were studied.The stress corrosion cracking sensitivity of the steel was low,and the fractography of its stress corrosion cracking showed transgranular and quasi-cleavage fracture with secondary cracks.The grade of anti-oxidization at 500℃ was very high.The surface of the steel was only slightly corroded after 500h salt-spray test,indicating that the steel had good anti-corrosion property.
中图分类号 TG174.2
所属栏目 试验研究
基金项目
收稿日期 2006/2/22
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: SUN Zhi-hua,ZHANG Xiao-yun,TANG Zhi-hui,LIU Ming-hui,GAO Jian,LIU Tian-qi,ZHI Min-xue. CORROSION PROPERTIES OF 0Cr13Ni8Mo2Al STAINLESS STEEL[J]. Corrosion & Protection, 2006, 27(12): 629～631
被引情况:
【1】黄春波,薛春,傅逸芳,张湛,王玲奇,周壹鸣, "PH13-8Mo不锈钢在3.5% NaCl溶液中的耐蚀性能",腐蚀与防护 34, 800-802(2013)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】AMS5629.宇航结构金属手册 pH 13-8Mo钢[M].1994.
【2】300M钢应力腐蚀研究技术总结[Z].北京航空材料研究院内部资料.1990.
【3】金属材料应力腐蚀开裂测试方法及其数据汇编[Z].北京航空材料研究院内部资料.1984.
【4】刚毅民.中国不锈钢腐蚀手册[M].北京:冶金工业出版社,1992.
【5】GB12445.3-1990高强度合金楔形张开加载(WOL)预裂纹试样应力腐蚀试验方法[S].
【6】HB5258-1983钢及高温合金的抗氧化性测定试验方法[S].
【7】ASTM B117-1979盐雾试验方法[S].
【8】HB5257-1983 腐蚀试验结果的重量损失测定和腐蚀产物的清除[S].
【2】300M钢应力腐蚀研究技术总结[Z].北京航空材料研究院内部资料.1990.
【3】金属材料应力腐蚀开裂测试方法及其数据汇编[Z].北京航空材料研究院内部资料.1984.
【4】刚毅民.中国不锈钢腐蚀手册[M].北京:冶金工业出版社,1992.
【5】GB12445.3-1990高强度合金楔形张开加载(WOL)预裂纹试样应力腐蚀试验方法[S].
【6】HB5258-1983钢及高温合金的抗氧化性测定试验方法[S].
【7】ASTM B117-1979盐雾试验方法[S].
【8】HB5257-1983 腐蚀试验结果的重量损失测定和腐蚀产物的清除[S].
相关信息