不同镀层的30CrMnSiA高强钢-TA15钛合金电偶腐蚀行为
GALVANIC CORROSION BEHAVIOR OF HIGH STRENGTH STEEL 30CrMnSiA WITH DIFFERENT ELECTROPLATINGS COUPLED WITH TITANIUM ALLOY TA15
摘 要
研究了3.5%NaCl溶液中,镀镍、镀镉钝化、镀锌钝化处理后的高强钢30CrMnSiA与TA15钛合金偶接后的电偶腐蚀行为.试验发现相比于镀镉钝化和镀锌钝化处理,镀镍处理的30CrMnSiA-TA15电偶对电偶腐蚀反应的驱动力最小,电偶电位最正,电偶电流密度最小,耐电偶腐蚀性能最好.采用扫描电镜观察电偶腐蚀后各种镀层的形貌,结果发现：镀镍层腐蚀形态为点蚀,镀镉钝化层会形成微裂纹,镀锌钝化层腐蚀局部呈片状,层层剥落.
高强钢30CrMnSiA
表面处理
电偶腐蚀
Titanium alloy TA15
High strength steel 30CrMnSiA
Surface treatment
Galvanic corrosion
Abstract
The effect of nickel-electroplating,cadmium-electroplating and passivating,zinc-electroplating and passivating treatment on galvanic corrosion of TA15-treated 30CrMnSiA couples was investigated in 3.5%NaCl solution.The plated film on 30CrMnSiA and the corrosion morphology were observed by SEM.Considering the value of open circuit potential difference,galvanic potential and galvanic current of the different galvanic couples,nickel-plated 30CrMnSiA had the best galvanic corrosion resistance.There were pits on nickel plating and micro-cracks on cadmium plating.The corrosion of zinc plating made it stripped as layers.
中图分类号 TG172.2
所属栏目 试验研究
基金项目
收稿日期 2006/10/30
修改稿日期 2006/11/16
网络出版日期
作者单位点击查看
引用该论文: LIU Jian-hua,YI Jun-lan,LI Song-mei,Xu Yong-zhen. GALVANIC CORROSION BEHAVIOR OF HIGH STRENGTH STEEL 30CrMnSiA WITH DIFFERENT ELECTROPLATINGS COUPLED WITH TITANIUM ALLOY TA15[J]. Corrosion & Protection, 2007, 28(7): 340～344
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】彭艳萍,曾凡昌,王俊杰,等.国外航空钛合金的发展应用及其特点分析[J].材料工程,1997(10):3-6.
【2】李兴无,沙爱学,张旺峰,等.TA15合金及其在飞机结构中的应用前景[J].钛工业进展,2003,20(4/5):90-94.
【3】鲍莉索娃著.陈石卿译.钛合金金相学[M].北京:国防工业出版社,1980.
【4】张晓云,孙志华,汤智慧,等.TA15钛合金与铝合金和结构钢接触腐蚀与防护研究[J].材料工程,2004(2):26-31.
【5】Nadia M,Taher,Abed S.Al Jabab.Galvanic corrosion behavior of implant suprastructure dental alloys[J].Dent Mater,2003,19:54-59.
【6】沈文雁,徐福源.Ti-15-3钛合金电偶腐蚀与防护研究[J].表面技术,1997,26(1):20-22.
【7】刘双梅,刘道新,樊国强.TA7钛合金/耐热不锈钢电偶腐蚀敏感性研究[J].材料工程,2000,1:17-30.
【8】张晓云,汤智慧,李斌,等.TB8钛合金电偶腐蚀与防护研究[J].材料工程,2001,376:171-173.
【9】张晓云,汤智慧,孙志华,等.0Cr13Ni8Mo2Al钢与铝合金和钛合金接触腐蚀与防护研究[J].腐蚀与防护,2002,23(10):423-426.
【10】王曰义.钛及其合金在流动海水中的腐蚀及对其他金属材料的电偶腐蚀作用[J].金属学报,2002,38:623-625.
【11】Brigitte Grosgogeat,Lucien Reclaru,Michele Lissac,et al.Measurement and evaluation of galvanic corrosion between titanium/Ti6Al4V implants and dental alloys by electrochemical techniques and auger spectrometry[J].Biomaterials,1999,20:933-941.
【12】Hassan Serhan,Michael Slivk,Todd Albert S.Daniel Kwak.Is galvanic corrosion between titanium alloy and stainless steel spinal implants a clinical concern[J].The Spine Journal,2004,4:379-387.
【13】刘建华,吴 昊,李松梅,等.高强合金与钛合金的电偶腐蚀行为[J].北京航空航天大学学报,2003,29(2):124-127.
【14】刘建华,吴 昊,李松梅,等.表面处理对TC2钛合金电偶腐蚀的影响[J].腐蚀科学与防护技术,2003,15(1):13-17.
【15】刘永辉,张佩芳.金属腐蚀学原理[M].北京:航空工业出版社,1993.
【2】李兴无,沙爱学,张旺峰,等.TA15合金及其在飞机结构中的应用前景[J].钛工业进展,2003,20(4/5):90-94.
【3】鲍莉索娃著.陈石卿译.钛合金金相学[M].北京:国防工业出版社,1980.
【4】张晓云,孙志华,汤智慧,等.TA15钛合金与铝合金和结构钢接触腐蚀与防护研究[J].材料工程,2004(2):26-31.
【5】Nadia M,Taher,Abed S.Al Jabab.Galvanic corrosion behavior of implant suprastructure dental alloys[J].Dent Mater,2003,19:54-59.
【6】沈文雁,徐福源.Ti-15-3钛合金电偶腐蚀与防护研究[J].表面技术,1997,26(1):20-22.
【7】刘双梅,刘道新,樊国强.TA7钛合金/耐热不锈钢电偶腐蚀敏感性研究[J].材料工程,2000,1:17-30.
【8】张晓云,汤智慧,李斌,等.TB8钛合金电偶腐蚀与防护研究[J].材料工程,2001,376:171-173.
【9】张晓云,汤智慧,孙志华,等.0Cr13Ni8Mo2Al钢与铝合金和钛合金接触腐蚀与防护研究[J].腐蚀与防护,2002,23(10):423-426.
【10】王曰义.钛及其合金在流动海水中的腐蚀及对其他金属材料的电偶腐蚀作用[J].金属学报,2002,38:623-625.
【11】Brigitte Grosgogeat,Lucien Reclaru,Michele Lissac,et al.Measurement and evaluation of galvanic corrosion between titanium/Ti6Al4V implants and dental alloys by electrochemical techniques and auger spectrometry[J].Biomaterials,1999,20:933-941.
【12】Hassan Serhan,Michael Slivk,Todd Albert S.Daniel Kwak.Is galvanic corrosion between titanium alloy and stainless steel spinal implants a clinical concern[J].The Spine Journal,2004,4:379-387.
【13】刘建华,吴 昊,李松梅,等.高强合金与钛合金的电偶腐蚀行为[J].北京航空航天大学学报,2003,29(2):124-127.
【14】刘建华,吴 昊,李松梅,等.表面处理对TC2钛合金电偶腐蚀的影响[J].腐蚀科学与防护技术,2003,15(1):13-17.
【15】刘永辉,张佩芳.金属腐蚀学原理[M].北京:航空工业出版社,1993.
相关信息