PROPERTIES OF CERAMIC COATING OBTAINED BY MICRO-ARC OXIDATION OF HOT-DIP ALUMINUM COATING ON Q235
摘 要
通过热浸镀铝后进行微弧氧化的方法在Q235钢表面获得一层陶瓷层,测定了微弧氧化陶瓷层的耐蚀性、耐磨性及硬度.结果表明无论是在NaCl溶液还是在海水中,陶瓷层的耐蚀性均优于热浸镀铝层.热浸镀铝层与陶瓷层都在10%NaCl溶液中的耐蚀性最差.陶瓷层的耐磨性显著优于经840 ℃淬火+150 ℃回火的45#钢,当摩擦延长米为70 m时,陶瓷层的耐磨性提高了2倍多.陶瓷层的硬度比基体提高了约10倍.
Abstract
The ceramic coating was obtained by the method of micro-arc oxidation of the hot-dip aluminum coating on Q235.The corrosion resistance,wear resistance,hardness of the ceramic coating were measured.The corrosion resistance of the micro-arc oxidized samples was much better than that of the hot-dip aluminum samples in either NaCl electrolyte or sea water.And the corrosion resistance of both the micro-arc oxidized samples and the hot-dip aluminum samples was worst in 10% NaCl electrolyte.The wear resistance of the ceramic coating was more than 3 times of the heat treated 45# steel when the wear distance was 70 meters.The hardness of the ceramic was about 11 times of the Q235 steel.
中图分类号 TG179
所属栏目 应用技术
基金项目
收稿日期 2006/9/4
修改稿日期 2006/10/14
网络出版日期
作者单位点击查看
引用该论文: LU Li-hong. PROPERTIES OF CERAMIC COATING OBTAINED BY MICRO-ARC OXIDATION OF HOT-DIP ALUMINUM COATING ON Q235[J]. Corrosion & Protection, 2007, 28(8): 425~426
被引情况:
【1】刘学文,柏其亚,李国朝, "氧化铝-氧化锆烧结陶瓷的耐海水腐蚀性能",腐蚀与防护 30, 459-461(2009)
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】薛文彬,邓志伟,来永春,等.铝合金微弧氧化陶瓷层的形成过程及其特征[J].电镀与精饰,1996,18(5):3-5.
相关信息