镁合金微弧氧化-电泳复合膜层的腐蚀性能
CORROSION PERFORMANCE OF MICRO-ARC-OXIDATION AND ELECTROPHORESIS COMPLEX COATINGS ON MAGNESIUM ALLOY
摘 要
镁合金微弧氧化-电泳复合处理作为新型的表面处理工艺,极大地提高了镁合金的耐蚀性,满足了工业化要求.通过考察在不同工艺条件下制备镁合金微弧氧化-电泳复合膜层的耐蚀性,研究其腐蚀机理,结果表明:微弧氧化-电泳复合膜层的耐蚀性取决于有机层的致密性以及复合膜层间的结合状态.致密性越好、结合力越大,复合膜层的耐蚀性越好.
微弧氧化-电泳
耐蚀性
腐蚀机理
Magnesium alloy
Micro-arc-oxidation and electrophoresis
Corrosion resistance
Corrosion mechanism
Abstract
The complex process technology of micro-arc-oxidation and electrophoresis is a new surface treatment method.The corrosion resistance of this complex coatings on magnesium alloy is reviewed and the corrosion mechanism is studied.The corrosion resistance of the complex coatings is determined by the compactness of organic layer and the combination state beween the complex coatings.The corrosion resistance of the complex coating is better when the compactness is better and the binding energy is bigger.
中图分类号 TG146.2+2 TG174.2
所属栏目 试验研究
基金项目 国家科技攻关项目(镁合金制品表面防护方法研究开发)项目编号:(2004BA311A14-1)
收稿日期 2006/11/9
修改稿日期 2006/11/20
网络出版日期
作者单位点击查看
引用该论文: SHI Hui-ying,YANG Wei,JIANG Bai-ling. CORROSION PERFORMANCE OF MICRO-ARC-OXIDATION AND ELECTROPHORESIS COMPLEX COATINGS ON MAGNESIUM ALLOY[J]. Corrosion & Protection, 2007, 28(9): 442～444
被引情况:
【1】王志平,郑晓,孙宇博, "纯铝微弧氧化-电泳膜层制备工艺及其耐蚀性",腐蚀与防护 31, 488-490(2010)
【2】杨华山,包晔峰,蒋永锋,杨可, "微弧氧化陶瓷层后处理技术的研究现状及展望",腐蚀与防护 31, 783-786(2010)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】陈振华.镁合金[M].化学工业出版社,2004:23-27.
【2】宋光铃.镁合金腐蚀与防护[M].化学工业出版社,2004:281-306.
【3】周义.电泳涂装新工艺[M].地质出版社,2004:10-15.
【4】陈平,王德中.环氧树脂及其应用[M].化学工业出版社,2002.
【5】洪啸吟,冯汉保.涂料化学[M].科学出版社,2005.
【6】黎完模,宋玉苏,邓淑珍,等.涂装金属的腐蚀[M].国防科技大学出版社,2003.
【7】卫中领,陈秋荣,丁翠红,等.镁合金微弧氧化膜的微观结构及耐蚀性研究[J].材料保护,2003,36(10):21-23.
【2】宋光铃.镁合金腐蚀与防护[M].化学工业出版社,2004:281-306.
【3】周义.电泳涂装新工艺[M].地质出版社,2004:10-15.
【4】陈平,王德中.环氧树脂及其应用[M].化学工业出版社,2002.
【5】洪啸吟,冯汉保.涂料化学[M].科学出版社,2005.
【6】黎完模,宋玉苏,邓淑珍,等.涂装金属的腐蚀[M].国防科技大学出版社,2003.
【7】卫中领,陈秋荣,丁翠红,等.镁合金微弧氧化膜的微观结构及耐蚀性研究[J].材料保护,2003,36(10):21-23.
相关信息