20#钢在三元复合驱弱碱体系采出液中的腐蚀与防护
The Corrosion and Protection of 20# Steel in Adopted Liquid of ASP Flooding Weak Alkali System
摘 要
通过室内配置模拟液和现场取样挂片试验,对腐蚀后的金属表面进行了形貌观察和表面元素分析,研究了20#钢在三元复合驱弱碱体系溶液中的腐蚀状况.结果表明,在模拟液中,20#钢腐蚀速率随三元组分浓度的提高而减缓；采出液在三元成分上返期间腐蚀速率略有增加,在0.244~0.271 mm/a之间.对油田常用内防腐涂层进行了室内静态模拟试验、动态环道试验和现场试验.结果表明,环氧粉末涂层具有较好的防腐蚀性能,其交流阻抗值在107 Ω·cm2以上,适用于三元复合驱弱碱体系.
弱碱体系
碳钢
涂层
电化学阻抗谱
ASP flooding
weak alkali system
carbon steel
coating
EIS
Abstract
The corrosion of 20# steel in adopted liquid of ASP(Alkali/Surfactant/Polymer) flooding weak alkali system was studied and the specimens were examined using scanning electron microscopy.In the simulated liquid,with the increase in concentrations of three components,the corrosion rate increased.The static simulation testing,dynamic loop test and field test showed that the corrosion protection properties of epoxy coating in ASP was relatively good.
中图分类号 TG172.6+3 TG174.46
所属栏目 试验研究
基金项目
收稿日期 2007/8/11
修改稿日期 2007/9/24
网络出版日期
作者单位点击查看
引用该论文: ZHU Dian-rui,LIU Xiao-dong,JI Peng-rong,HE Shu-quan. The Corrosion and Protection of 20# Steel in Adopted Liquid of ASP Flooding Weak Alkali System[J]. Corrosion & Protection, 2008, 29(2): 71～73
被引情况:
【1】程浩力,刘德俊, "A3、20#和X70钢室内模拟流动海水腐蚀试验",腐蚀与防护 33, 212-215(2012)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】赵长久,赵群,么世椿.弱碱三元复合驱与强碱三元复合驱的对比[J].新疆石油地质,2006,27(6):728-730.
【2】韩霞.Q235钢在三元驱油剂介质中的腐蚀特性研究[J].腐蚀与防护,2003,24(5):192-196.
【3】曹楚南.腐蚀电化学[M].化学工业出版社,1994.
【2】韩霞.Q235钢在三元驱油剂介质中的腐蚀特性研究[J].腐蚀与防护,2003,24(5):192-196.
【3】曹楚南.腐蚀电化学[M].化学工业出版社,1994.
相关信息