RTM成型技术在码头钢筋混凝土结构修复中的应用
Application of RTM Technology to Reinforced Concrete Repair Engineering of Dock
摘 要
采用树脂传递模塑工艺Resin Transfer Molding(RTM)对上海石化热电总厂煤码头钢筋混凝土结构进行填充修复和防腐蚀处理.分析了钢筋混凝土材料的腐蚀以及RTM成型工艺的关键因素:钢筋混凝土的失效主要是由于Cl-渗入混凝土内部而导致钢筋材料发生电化学腐蚀,而树脂料对增强材料浸润能力以及铺设技术对RTM成型工艺都有直接的影响.通过RTM成型对受损码头进行填充修复,明显提高了结构承载和改善其外观.
钢筋混凝土
腐蚀机理
码头
浸润能力
RTM
reinforced concrete
corrosion mechanism
dock
wetting capability
Abstract
The processes of filling and anti-corrosion to the reinforced concrete of Shanghai Petrochemical Thermoelectricity Corporation’s dock were performed by RTM technology,and the corrosion mechanism of the reinforced concrete and the factors of RTM technology were analyzed.The failure of the reinforced concrete was largely due to the penetration of Cl- into the concrete,leading to electrochemical corrosion of the reinforcing steel bar.However,the wetting capability of the resin to reinforced materials and the paving methods had obvious influence on the RTM technology.The filling to the damaged dock by RTM improved the structural bearing apacity and the appearance of the dock.
中图分类号 TU746
所属栏目 应用技术
基金项目
收稿日期 2007/4/19
修改稿日期 2007/5/16
网络出版日期
作者单位点击查看
引用该论文: HE Bin,YANG Zhen-guo,JING Yong-wei,XU Kai. Application of RTM Technology to Reinforced Concrete Repair Engineering of Dock[J]. Corrosion & Protection, 2008, 29(2): 92～94
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】王柏臣,黄玉东.树脂传递模塑(RTM)工艺树脂微观流动行为数值分析[J].固体火箭技术,2006,29(4):297-300.
【2】陈祥宝.先进树脂基复合材料的发展[J].航空材料学报,2000,20(1):46-54.
【3】F Abali,Shivakumar,K Hamidi N.An RTM densification method of manufacturing carbon-carbon composites using primaset PT-30 resin[J].Carbon,2003,41:893-901.
【4】胡平,刘锦霞.酚醛树脂及其复合材料成型工艺的研究进展[J].热固性树脂,2006,21(1):36-41.
【5】陈有治,徐瑛.酸性介质对钢筋混凝土腐蚀机理研究[J].武汉理工大学学报,2001,23(8):4-6.
【6】张宏,解宏伟.盐湖地区混凝土腐蚀机理及防护措施[J].青海科技,2006(3):48-49.
【7】陈惠玲,李晓娟,魏雨,等.碳钢在含氯离子环境中的腐蚀机理的研究[J].腐蚀与防护,2007,28(1):17-19.
【8】刘钧,曾竟成.RTM注射成型列车机车用复合材料车门/窗框[J].纤维复合材料,2002(3):3-4.
【2】陈祥宝.先进树脂基复合材料的发展[J].航空材料学报,2000,20(1):46-54.
【3】F Abali,Shivakumar,K Hamidi N.An RTM densification method of manufacturing carbon-carbon composites using primaset PT-30 resin[J].Carbon,2003,41:893-901.
【4】胡平,刘锦霞.酚醛树脂及其复合材料成型工艺的研究进展[J].热固性树脂,2006,21(1):36-41.
【5】陈有治,徐瑛.酸性介质对钢筋混凝土腐蚀机理研究[J].武汉理工大学学报,2001,23(8):4-6.
【6】张宏,解宏伟.盐湖地区混凝土腐蚀机理及防护措施[J].青海科技,2006(3):48-49.
【7】陈惠玲,李晓娟,魏雨,等.碳钢在含氯离子环境中的腐蚀机理的研究[J].腐蚀与防护,2007,28(1):17-19.
【8】刘钧,曾竟成.RTM注射成型列车机车用复合材料车门/窗框[J].纤维复合材料,2002(3):3-4.
相关信息