MB2镁合金SiO2基陶瓷涂层的性能
Properties of SiO2-based Ceramic Coating on MB2 Magnesium Alloy
摘 要
采用热化学反应法在MB2镁合金上制备了SiO2基陶瓷涂层.并从微观结构、抗热震性、耐磨和耐蚀性能等方面测试涂层性能.试验结果表明:涂层中有新相MgMnSiO4生成,涂层与基体结合强度较高,耐磨和耐腐蚀性能优异.
陶瓷涂层
热化学反应
耐腐蚀性
MB2 magnesium alloy
ceramic coating
thermo-chemical reaction
corrosion resistance
Abstract
SiO2-based ceramic coating was prepared on MB2 magnesium alloy by thermo-chemical reaction.Coating performance was tested from the micro-structure,thermal shock resistance,wear resistance and corrosion resistance and so on.A new phase of MgMnSiO4 was generated.There was a relatively high combination strength between coating and substrate,and the coating had good wear and corrosion resistance.
中图分类号 TG174.45
所属栏目 试验研究
基金项目 辽宁省自然科学基金资助项目(20062203)
收稿日期 2007/8/25
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: SHI Hai-fang,LI Xiao,MA Zhuang,LI Zhi-chao. Properties of SiO2-based Ceramic Coating on MB2 Magnesium Alloy[J]. Corrosion & Protection, 2008, 29(8): 457～459
被引情况:
【1】温玉清,尚伟,李晓晓,蒋秀娟, "pH值对镁合金表面氧化硅溶胶凝胶成膜及膜层性能的影响",腐蚀与防护 32, 477-479(2011)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】卢屹东,亢世江,丁敏.金属表面陶瓷涂层的技术特点及应用[J].焊接技术,2005,34(2):7-9.
【2】穆柏春,张丽娟,谷志刚.耐热防腐蚀复相陶瓷涂层的研究[J].材料保护,1997,6(30):24-25.
【3】金华兰,韩丽华.镁及其合金表面化学改性技术[J].轻合金加工技术,2005(12):29-33.
【2】穆柏春,张丽娟,谷志刚.耐热防腐蚀复相陶瓷涂层的研究[J].材料保护,1997,6(30):24-25.
【3】金华兰,韩丽华.镁及其合金表面化学改性技术[J].轻合金加工技术,2005(12):29-33.
相关信息