摘 要
通过盐雾试验和点腐蚀电位测试,对比了新型940X不锈钢和9Cr18不锈钢的耐蚀性能.结果表明,在NaCl溶液中940X不锈钢的耐全面腐蚀和耐点腐蚀的性能比9Cr18的高.并结合化学成分及金相能谱分析了940X不锈钢的耐蚀机理.
Abstract
The corrosion resistance of stainless steels 940X and 9Cr18 was investigated by salt spraying tests and pitting potential measurements.Results show that the general corrosion and pitting corrosion resistance of stainless steel 940X was better than that of stainless steel 9Cr18.The mechanism of corrosion resistance of stainless steel 940X was also discussed based on SEM and EDS analyses.
中图分类号 TG142.7 TG174.2
所属栏目 试验研究
基金项目 上海市应用技术开发专项资金资助项目(05-011)
收稿日期 2008/3/9
修改稿日期 2008/6/10
网络出版日期
作者单位点击查看
引用该论文: LIU Xiao-ning,HUANG Chun-bo,SHEN Zhong-liang,XUE-Chun. Corrosion Resistance of New Stainless Steel 940X[J]. Corrosion & Protection, 2008, 29(9): 523~525
被引情况:
【1】霍世军,孙博,苏敬, "9Cr18合金的燃气热腐蚀行为",理化检验-物理分册 52, 95-98(2016)
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】罗家英,朱祖昌.我国轴承钢的现状与发展概况[J].热处理,2002,17(3):44-50.
【2】俞峰,魏果能,许达.不锈轴承材料的研究和发展[J].钢铁研究学报,2005,17(1):6-9.
【3】王玉金,叶键槢.常用不锈轴承钢的设计要点与材料[J].轴承,2004(12):37-39.
【4】叶键槢.,高元安,仇亚军,等.滚动轴承常用金属材料[J].工艺与装备,2005(8):96-98.
【2】俞峰,魏果能,许达.不锈轴承材料的研究和发展[J].钢铁研究学报,2005,17(1):6-9.
【3】王玉金,叶键槢.常用不锈轴承钢的设计要点与材料[J].轴承,2004(12):37-39.
【4】叶键槢.,高元安,仇亚军,等.滚动轴承常用金属材料[J].工艺与装备,2005(8):96-98.
相关信息