Urotropine as a Corrosion Inhibitor in Hydrochloric Acid Solution
摘 要
采用挂片失重法研究了乌洛托品在不同浓度和温度下在盐酸清洗剂中对碳钢的缓蚀行为.结果表明:随着缓蚀剂乌洛托品浓度的增大,其浓度为1.5%时,缓蚀效率出现最大值,大于该浓度后,缓蚀效率下降;随着温度升高,乌洛托品的缓蚀作用效果降低.试验结果与工程实践结果相符.
Abstract
The corrosion inhibition and adsorption behavior of urotropine for carbon steel in a hydrochloric acid solution were studied by wetght loss method.The results showed that with increasing urotropine concentration to 1.5%,the maximum of inhibition efficiency was observed.When the concentration of urotropine was greater than 1.5% and with temperature increasing,urotropine made inhibition efficiency decreased.The experimental result is conformed to the engineering practice.
中图分类号 TG174.42
所属栏目 试验研究
基金项目
收稿日期 2008/2/13
修改稿日期 2008/3/20
网络出版日期
作者单位点击查看
引用该论文: GAO Jun-lin. Urotropine as a Corrosion Inhibitor in Hydrochloric Acid Solution[J]. Corrosion & Protection, 2009, 30(3): 182~183
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】梁治齐.实用清洗技术手册[M].北京:化学工业出版社,2005:115.
【2】徐永成.钢铁盐酸除锈常用添加剂及应用[J].四川冶金,1994(2):49-50.
【3】曾荣昌,韩恩厚.材料的腐蚀与防护[M].北京:化学工业出版社,2006:296.
【4】王保成,朱金华.盐酸溶液中乌鲁托品对钢的缓蚀性能[J].北京科技大学学报,2006,28(3):259-262.
【5】周琼花,杨道武,朱志平.钨酸盐与乌洛托品对碳钢协同缓蚀作用的研究[J].华北电力技术,2004(3):3-5.
【6】周勇.对混酸金属除锈液中添加剂的缓蚀和去锈作用的研究[J].化学工程师,2000,79(4):44-46.
【7】张健,杜光军,杨志弘,等.六次甲基四胺自盐酸溶液中在钢表面上的吸附[J].中南民族学院学报(自然科学版),1998,17(l):26-28.
【8】于建辉,彭乔,崔元成.膦羧酸型缓蚀阻垢剂的缓蚀行为研究[J].材料保护,2004,37(7):42-43.
【2】徐永成.钢铁盐酸除锈常用添加剂及应用[J].四川冶金,1994(2):49-50.
【3】曾荣昌,韩恩厚.材料的腐蚀与防护[M].北京:化学工业出版社,2006:296.
【4】王保成,朱金华.盐酸溶液中乌鲁托品对钢的缓蚀性能[J].北京科技大学学报,2006,28(3):259-262.
【5】周琼花,杨道武,朱志平.钨酸盐与乌洛托品对碳钢协同缓蚀作用的研究[J].华北电力技术,2004(3):3-5.
【6】周勇.对混酸金属除锈液中添加剂的缓蚀和去锈作用的研究[J].化学工程师,2000,79(4):44-46.
【7】张健,杜光军,杨志弘,等.六次甲基四胺自盐酸溶液中在钢表面上的吸附[J].中南民族学院学报(自然科学版),1998,17(l):26-28.
【8】于建辉,彭乔,崔元成.膦羧酸型缓蚀阻垢剂的缓蚀行为研究[J].材料保护,2004,37(7):42-43.
相关信息