An Alkalescency Electroplating Technology of Zn-Ni Alloy
摘 要
探究了一种光亮碱性锌镍合金的电镀工艺,镀液的基本组成为:ZnO,NiSO4,NaOH和三乙醇胺.采用中性盐雾试验方法测量了两种不同的钝化层的耐蚀性能.结果表明,低铬彩色钝化工艺,获得了光亮度好、连续的彩色钝化膜,具有较高的耐腐蚀性能.
Abstract
An alkalescency electroplating technology of Zn-Ni Alloy was studied .The alkaline plating bath of zine-nickel alloy contained ZnO,NiSO4,NaOH and triethanolamine(TEA).The corrosion resistance of Zn-Ni alloy coating layer after two different kinds of passivation was studied by salt spray testing.The results showed that low-chrome colorful passivation could form a bright and consecutive film with excellent corrosion resistance.
中图分类号 TQ153.2
所属栏目 应用技术
基金项目
收稿日期 2008/3/11
修改稿日期 2008/10/13
网络出版日期
作者单位点击查看
引用该论文: CHEN Guo-xing,XIONG Zhen-xing,ZHAO Ke-xin,FU Chuan-feng. An Alkalescency Electroplating Technology of Zn-Ni Alloy[J]. Corrosion & Protection, 2009, 30(3): 196~197
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】屠振密,张景双,杨哲龙.环保无害化电镀的研究进展[J].材料保护,2001,34(8):1-3.
【2】屠振密.电镀合金原理与工艺[M].北京:国防工业出版社,1993:212-213.
【2】屠振密.电镀合金原理与工艺[M].北京:国防工业出版社,1993:212-213.
相关信息