合成咪唑啉缓蚀剂在油田水中的模拟试验
Synthesizing and Simulating Corrosion Test of Imidazoline in Oilfield Water
摘 要
根据塔河油田采油一厂输油管线腐蚀现状,在实验室合成了一种咪唑啉衍生物缓蚀剂,并通过室内浸泡试验和电化学测试分析了该缓蚀剂的缓蚀机理.
腐蚀
油田
imidazoline
corrosion
oildfiled
Abstract
An imidazoline derivative as an inhibitor for the oilfield water was synthesized in laboratory,and its inhibition efficiency and inhibition mechanism were studied by means of electrochemical methods.
中图分类号 TG174.42
所属栏目 试验研究
基金项目
收稿日期 2009/1/17
修改稿日期 2009/2/26
网络出版日期
作者单位点击查看
引用该论文: XING Jing. Synthesizing and Simulating Corrosion Test of Imidazoline in Oilfield Water[J]. Corrosion & Protection, 2009, 30(5): 322～324
被引情况:
【1】上官昌淮,王霞,杜磊,殷名学,李科, "一种咪唑啉缓蚀剂的合成及缓蚀性能评价",腐蚀与防护 32, 528-531(2011)
【2】左秀丽,舒建华,王志民,何天稀, "高氯油田水溶液中咪唑类缓蚀剂的性能",腐蚀与防护 36, 148-151(2015)
【3】王霞,上官昌淮,陈玉祥, "温度对咪唑啉缓蚀剂成环程度及缓蚀性能的影响",腐蚀与防护 32, 21-23(2011)
【4】赵旭辉,王芳,周勇,唐聿明,左禹, "咪唑啉季铵盐对A3碳钢在NaNO2+NaCl溶液中点蚀行为的影响",腐蚀与防护 36, 113-117(2015)
【5】王彬,杜敏,张静, "油气田中抑制CO2腐蚀缓蚀剂的应用及其研究进展",腐蚀与防护 31, 503-507(2010)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】Guoan Zhang,Changfeng Chen,Minxu Lu,et al.Evaluation of inhibition efficiency of an imidazoline derivative in CO2-containing aqueous solution[J].Materls Chemistry and Physics,2007,105:331-340.
【2】Cruz J,R Martínez,J Genesca,et al.Experimental and theoretical study of 1-(2-ethylamino)-2-methylimidazoline as an inhibitor of carbon steel corrosion in acid media[J].Joural of Electroanalytical Chemistry,2004,566:111-121.
【3】López D A,W H Schreiner,S R de Sánchez,et al.The influence of inhibitors molecular structure and steel microstructure on corrosion layers in CO2 corrosion an XPS and SEM characterization[J].Applied Surface Science,2004,235:77-97.
【2】Cruz J,R Martínez,J Genesca,et al.Experimental and theoretical study of 1-(2-ethylamino)-2-methylimidazoline as an inhibitor of carbon steel corrosion in acid media[J].Joural of Electroanalytical Chemistry,2004,566:111-121.
【3】López D A,W H Schreiner,S R de Sánchez,et al.The influence of inhibitors molecular structure and steel microstructure on corrosion layers in CO2 corrosion an XPS and SEM characterization[J].Applied Surface Science,2004,235:77-97.
相关信息