Corrosion Resistance of Three Kinds of Ni-base Alloy Electroless Plating Layer
摘 要
本工作沉积出了高磷含量的Ni-P合金镀层和Ni-W-P 、Ni-W-P/Pr2O3镀层.利用浸泡试验对比了三种镀层在5% NaCl溶液中的耐蚀性能,利用极化曲线法对比了三种镀层在3.5% NaCl水溶液中的腐蚀电化学行为.结果表明,三元合金镀层具有比二元合金镀层更优异的耐蚀性能,三元合金镀层在添加稀土后耐蚀性能进一步提高.镀层的低孔隙和易钝化现象是其耐蚀性能高的重要原因.
Abstract
Three kinds of electroless Ni-P plating with high P content,Ni-W-P and Ni-W-P/Pr2O3 were prepared.The corrosion resistance of the three kinds of plating was compared using immersion experiment in 5% NaCl.The corrosion electrochemical behaviors in 3.5% NaCl solution of the three kinds of plating were tested by polarization curves.The results showed that the Ni-W-P/Pr2O3 plating was the best,and Ni-P film was the worst.The corrosion current densities of Ni-W-P and Ni-W-P/Pr2O3 platings were 3.863 μA/cm2 and 2.977 μA/cm2,much smaller than that of the Ni-P film,which was 10.11 μA/cm2.The ternary alloy plating have more excellent corrosion resistance than binary alloy plating.The corrosion resistance of ternary alloy plating could be improved by adding rare earth.The low porosity and easy passivation are the important reasons for high corrosion resistance.
中图分类号 TG153.2
所属栏目 试验研究
基金项目
收稿日期 2008/5/12
修改稿日期 2008/9/9
网络出版日期
作者单位点击查看
备注许晓丽,讲师.
引用该论文: XU Xiao-li,FAN Jun-guo,LI Su-mei,HOU Ya-wei. Corrosion Resistance of Three Kinds of Ni-base Alloy Electroless Plating Layer[J]. Corrosion & Protection, 2009, 30(6): 392~393
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】王霞,彭健锋, 陈玉祥,等.化学镀Ni-P合金耐蚀性能优化的研究方向[J].表面技术,2006,35(4):9-12.
【2】姜晓霞,沈伟.化学镀理论及实践[M].北京:国防工业出版社,2000.102-109.
【3】闫洪.现代化学镀镍和复合镀新技术[M].国防工业出版社,1999(2):82-83.
【4】李卫清,董人瑞,傅雅琳,等.稀土元素化学镀镍工艺研究[J].材料保护,1998,31(7):12-13.
【2】姜晓霞,沈伟.化学镀理论及实践[M].北京:国防工业出版社,2000.102-109.
【3】闫洪.现代化学镀镍和复合镀新技术[M].国防工业出版社,1999(2):82-83.
【4】李卫清,董人瑞,傅雅琳,等.稀土元素化学镀镍工艺研究[J].材料保护,1998,31(7):12-13.
相关信息