高温合金零件电刷镀时的腐蚀问题
Corrosion of High-temperature Alloy Parts in Brush Plating
摘 要
分析了高温合金零件电刷镀时可能出现的腐蚀原因.通过工艺试验模拟了各种可能出现零件表面腐蚀的情况.结果表明,零件与夹具之间的导电性问题是腐蚀的主要原因,零件与夹具间形成的缝隙中有无镀液会改变腐蚀类型,只要保证导电性良好,在操作时间内零件不会发生明显的缝隙腐蚀.
电刷镀
腐蚀
导电性
high-temperature alloy
brush plating
corrosion
conductivity
Abstract
The corrosion reasons of high-temperature alloy parts in brush plating were analyzed.The corrosion conditions were simulated by technical experiments.Results showed that the electric conductivity between alloy parts and tongs was the primary corrosion reason.The plating solution in the crevice could bring different types of corrosion.Under good conductivity condition,obvious crevice corrosion would not appear in brush plating.
中图分类号 TQ153 TG174
所属栏目 应用技术
基金项目
收稿日期 2008/5/30
修改稿日期 2008/6/20
网络出版日期
作者单位点击查看
引用该论文: HUANG Xuan-Min,XIN Zhe-Kuan,HU bing,GAO Sheng-Wen,TANG En-Jun. Corrosion of High-temperature Alloy Parts in Brush Plating[J]. Corrosion & Protection, 2009, 30(6): 414～416
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】颜鸣皋.中国航空材料手册[M].北京:中国标准出版社,2002.
【2】魏宝明.金属腐蚀理论及应用[M].南京:化学工业出版社,1982.
【3】郭鹤桐,刘淑兰.理论电化学[M].天津:宇航出版社,1983.
【2】魏宝明.金属腐蚀理论及应用[M].南京:化学工业出版社,1982.
【3】郭鹤桐,刘淑兰.理论电化学[M].天津:宇航出版社,1983.
相关信息