pH值对热镀锌汽车板和IF钢基板在NaCl溶液中电化学行为的影响
Influence of pH on Electrochemical Behaviors of Hot-dip Galvanized Auto Steel Sheet and IF Substrate in NaCl Solutions
摘 要
通过电化学阻抗谱(EIS)和极化曲线测量,研究了pH值对热镀锌汽车板和IF钢(无间隙原子钢)基板在5% NaCl溶液中电化学腐蚀行为的影响.结果表明:在三种不同pH值的溶液中,镀锌板的腐蚀过程主要受电荷传递过程控制,而基板的腐蚀过程受氧和氢离子的扩散过程控制.虽然镀锌板的腐蚀速度比基板的腐蚀速度快,但腐蚀过程都呈现了相似的变化趋势,都是随着pH值的增大,电荷转移电阻逐渐增大,腐蚀电流密度依次减小,即腐蚀速度依次减小.
热镀锌汽车板
IF钢(无间隙原子钢)
NaCl溶液
电化学腐蚀
pH value
hot-dip galvanized auto steel sheet
IF(interstitial-free) steel
NaCl solution
electrochemical corrosion
Abstract
Electrochemical behaviors of the hot-dip galvanized auto steel sheet and IF (interstitial-free) substrate were investigated by means of EIS and polarization curves in NaCl solutions with various pH values.The results showed that the corrosion process of the galvanized steel sheet was mainly controlled by charge transfer process,but corrosion of the IF substrate was controlled by the diffusion process of oxygen and hydrogen ions in the solutions.The galvanized steel presented a higher corrosion rate than the IF steel substrate,but the corrosion evolution tendencies were similar.With increasing the pH value the charge transfer resistance increased,and thus the corrosion current density decreased,i.e.,the corrosion rate decreased gradually.
中图分类号 TG172.6
所属栏目 试验研究
基金项目 国家自然科学基金项目(No.50571022);国家科技基础条件平台建设资助项目(No.2005DKA10400)
收稿日期 2008/7/16
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: ZHANG Hong,DU Cui-wei,QI Hui-bin,LI Xiao-gang. Influence of pH on Electrochemical Behaviors of Hot-dip Galvanized Auto Steel Sheet and IF Substrate in NaCl Solutions[J]. Corrosion & Protection, 2009, 30(7): 451～453
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】李明齐,何晓英,蔡铎昌,等.16Mn钢在NaCl薄层液膜下腐蚀的电化学研究[J].吉林化工学院学报,2003,20(2):65-67.
【2】曹楚南,张鉴清.电化学阻抗谱导论[M].北京:科学出版社,2002:21-93.
【3】安百钢,张学元,韩恩厚,等.Zn在模拟酸雨溶液中及其液膜下的腐蚀[J].金属学报,2004,40(2):202-206.
【4】Zhao J M,Zuo Y.Corrosion behavior in simulated solutions within pits and crevices on carbon steel[J].Corrosion Engineering,Science and Technology,2007,42(3):203-206.
【5】Keddam M,Hugotlegoff A,Takenouti H,et al.The influence of a thin electrolyte layer on the corrosion process of zinc in chloride-containing solutions[J].Corrosion Science,1992,33(8):1243-1252.
【6】杨熙珍,杨 武.金属腐蚀电化学热力学电位-pH图及其应用[M].北京:化学工业出版社,1991:106-107.
【7】安百钢,张学元,韩恩厚,等.A3钢在模拟降雨环境下的腐蚀和冲刷行为研究[J].金属学报,2002,38(7):755-759.
【8】刁兆玉,韩允雨,李怀祥.铁在酸碱及氯离子介质中腐蚀的研究[J].山东师大学报,2000,15(3):274-278.
【2】曹楚南,张鉴清.电化学阻抗谱导论[M].北京:科学出版社,2002:21-93.
【3】安百钢,张学元,韩恩厚,等.Zn在模拟酸雨溶液中及其液膜下的腐蚀[J].金属学报,2004,40(2):202-206.
【4】Zhao J M,Zuo Y.Corrosion behavior in simulated solutions within pits and crevices on carbon steel[J].Corrosion Engineering,Science and Technology,2007,42(3):203-206.
【5】Keddam M,Hugotlegoff A,Takenouti H,et al.The influence of a thin electrolyte layer on the corrosion process of zinc in chloride-containing solutions[J].Corrosion Science,1992,33(8):1243-1252.
【6】杨熙珍,杨 武.金属腐蚀电化学热力学电位-pH图及其应用[M].北京:化学工业出版社,1991:106-107.
【7】安百钢,张学元,韩恩厚,等.A3钢在模拟降雨环境下的腐蚀和冲刷行为研究[J].金属学报,2002,38(7):755-759.
【8】刁兆玉,韩允雨,李怀祥.铁在酸碱及氯离子介质中腐蚀的研究[J].山东师大学报,2000,15(3):274-278.
相关信息