镁合金稀土镧化学转化工艺研究
Rare Earth Lanthanum Conversion Treatment of Magnesium Alloy
摘 要
镁合金稀土转化膜技术是近年来发展起来的一种环保型镁合金表面处理新技术.通过正交试验对压铸镁合金AZ91D稀土镧化学转化处理工艺进行了研究.利用扫描电子显微镜(SEM)、能量色散谱(EDS)和X射线光电子能谱(XPS)研究了膜层的表面形貌及其组成,并通过容量法对膜层在5% NaCl(pH=6.8~7.0)溶液中的耐腐蚀性能进行了研究.结果表明:La转化处理工艺能够在压铸镁合金AZ91D表面形成均匀、完整的转化膜;膜层主要由La2O3和MgO以及少量的Al2O3组成;La转化膜在浸泡初期的10 h内耐腐蚀性能与铬酸盐转化膜相当.
镧
稀土转化
耐腐蚀性
magnesium alloy
lanthanum
rare earth conversion
corrosion resistance
Abstract
Rare earth conversion coatings on magnesium alloys have been developed as an environmental-friendly surface treatment technology for magnesium alloys.The process of rare earth lanthanum conversion coating for magnesium alloy AZ91D was studied by using orthogonal test.The surface morphology and composition of lanthanum conversion coating were studied by means of scanning electron microscopy (SEM),energy dispersive spectroscopy (EDS) and X-ray photoelectron spectroscopy (XPS).The corrosion resistance of magnesium alloy in 5% NaCl solutions with pH 6.8~7.0 was analyzed by evolving hydrogen gas measurement.The results showed that uniform coating by the process of lanthanum conversion was obtained on Mg alloy.The lanthanum conversion coating was mainly composed of MgO,La2O3 and a little amount of Al2O3.During immersion in 5% NaCl solution for 10 h,the corrosion resistance of lanthanum conversion coating was comparable with that of chromate conversion coating.
中图分类号 TG178 TG146
所属栏目 试验研究
基金项目 航空科学基金资助项目(03H51016);中国计量学院引进人才科研启动项目(01101-149);国家自然科学基金项目(50702054)
收稿日期 2008/7/25
修改稿日期 2008/9/28
网络出版日期
作者单位点击查看
引用该论文: BAI Li-qun,QIAN Jian-gang,SHU Kang-ying,LI Di. Rare Earth Lanthanum Conversion Treatment of Magnesium Alloy[J]. Corrosion & Protection, 2009, 30(7): 46～469
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】焦树强,旷亚非,陈金华,等.镁及其合金的腐蚀与阳极化处理[J].电镀与环保,2002,22(3):1-4.
【2】曾爱平,薛颖,钱宇峰,等.镁合金的化学表面处理[J].腐蚀与防护,2002,21(2):55-56.
【3】Rudd A L,Breslin C B,Mansfeld F.The corrosion protection afforded by rare earth conversion coatings applied to magnesium[J].Corrosion Science,2000,42(2):275-288.
【4】Montemor M F,Simes A M,Carmezim M J.Characterization of rare-earth conversion films formed on the AZ31 magnesium alloy and its relation with corrosion protection[J].Applied Surface Science,2007,253:6922-6931.
【5】Dabala M,Brunelli K,Napolitani E,et al.Cerium-based chemical conversion coating on AZ63 magnesium alloy[J].Surface and Coatings Technology,2003,172:227-232.
【6】张永君,严川伟,王福会.Mg及Mg合金表面稀土转化处理及其耐蚀性研究[J].腐蚀科学与防护技术,2001,13(增刊):467-470.
【7】许越,陈湘,吕祖舜,等.AZ91镁合金表面稀土转化膜的制备及耐蚀性能研究[J].中国稀土学报,2005,23(1):40-43.
【8】Yu Shengxue,Zhang Zhanwei,Chen Ling,et al.Influence of solution composition formation of golden yellow rare earth conversion film on magnesium alloy[J].Journal of Rare Earths,2005,23(S):255-258.
【9】Yu Shengxue,LV Qianyan,HAN Jing,et al.Preparation and performance of rare earths chemical conversion film on magnesium alloy[J].Journal of Rare Earth,2006,24:397-400.
【10】Zheng R F,Liang C H.Conversion coating treatment for AZ91 magnesium alloys by a permanganate-REMS bath[J].Materials and Corrosion,2007,58(3):193-197.
【11】陈东初,吴桂香,李炜常,等.AZ91D镁合金无铬铈盐转化膜的正交试验研究[J].轻合金加工技术,2007,35(6):43-47.
【12】王建祺,吴文辉,冯大明.电子能谱学(XPS/XAES/UPS)引论[M].北京:国防工业出版社,1992.
【2】曾爱平,薛颖,钱宇峰,等.镁合金的化学表面处理[J].腐蚀与防护,2002,21(2):55-56.
【3】Rudd A L,Breslin C B,Mansfeld F.The corrosion protection afforded by rare earth conversion coatings applied to magnesium[J].Corrosion Science,2000,42(2):275-288.
【4】Montemor M F,Simes A M,Carmezim M J.Characterization of rare-earth conversion films formed on the AZ31 magnesium alloy and its relation with corrosion protection[J].Applied Surface Science,2007,253:6922-6931.
【5】Dabala M,Brunelli K,Napolitani E,et al.Cerium-based chemical conversion coating on AZ63 magnesium alloy[J].Surface and Coatings Technology,2003,172:227-232.
【6】张永君,严川伟,王福会.Mg及Mg合金表面稀土转化处理及其耐蚀性研究[J].腐蚀科学与防护技术,2001,13(增刊):467-470.
【7】许越,陈湘,吕祖舜,等.AZ91镁合金表面稀土转化膜的制备及耐蚀性能研究[J].中国稀土学报,2005,23(1):40-43.
【8】Yu Shengxue,Zhang Zhanwei,Chen Ling,et al.Influence of solution composition formation of golden yellow rare earth conversion film on magnesium alloy[J].Journal of Rare Earths,2005,23(S):255-258.
【9】Yu Shengxue,LV Qianyan,HAN Jing,et al.Preparation and performance of rare earths chemical conversion film on magnesium alloy[J].Journal of Rare Earth,2006,24:397-400.
【10】Zheng R F,Liang C H.Conversion coating treatment for AZ91 magnesium alloys by a permanganate-REMS bath[J].Materials and Corrosion,2007,58(3):193-197.
【11】陈东初,吴桂香,李炜常,等.AZ91D镁合金无铬铈盐转化膜的正交试验研究[J].轻合金加工技术,2007,35(6):43-47.
【12】王建祺,吴文辉,冯大明.电子能谱学(XPS/XAES/UPS)引论[M].北京:国防工业出版社,1992.
相关信息