2205双相不锈钢在卤水环境中的腐蚀行为
Corrosion Behavior of 2205 Duplex Stainless Steel in Bittern
摘 要
根据实际的制盐工艺条件,使用单因素试验和均匀试验,采用电化学测试方法,研究了2205双相不锈钢在不同的S2-浓度、CO2-3浓度、pH值和流速的盐卤介质中的腐蚀行为.结果表明,在盐卤介质中S2-浓度和pH值对2205DSS的耐蚀性能影响较大,而CO2-3浓度和流速对其影响较小.
卤水环境
点蚀
均匀设计试验
电化学测试
2205DSS
Bittern
Pitting
Uniform experiment
electrochemical test
Abstract
Accordding to the actual process of salt making,the corrosion behaviors of 2205 duplex stainless steel in bittern solutions with different CO2-3 concentrations,S2- concentrations,pH values and flow velocities were studied by single factor experiment,uniform experiment and electro chemical test.The results showed that S2- concentration and pH value had great influences on corrosion resistance of 2205DSS in bittern,and CO2-3 concentration and flow rate had little influence.
中图分类号 TG172.6
所属栏目 试验研究
基金项目
收稿日期 2008/7/10
修改稿日期 2008/7/14
网络出版日期
作者单位点击查看
联系人作者邹振(zc736@163.com)
引用该论文: GONG Min,ZOU Zhen,ZHENG Xing-wen,HUANG Wen-heng,ZHAO Fang. Corrosion Behavior of 2205 Duplex Stainless Steel in Bittern[J]. Corrosion & Protection, 2009, 30(7): 473～476
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】Ikeda A,Veda M,Mukal S.CO2 Corrosion Behavior and Mechanism of Carbon Steel and Alloy Steel[C]//Corrosion Paper,NACE,1983:45-48.
【2】葛红花,周国定,吴文权.硫离子对316L不锈钢耐蚀性的影响[J].华北电力技术,2003(8):46-49.
【3】周琦,王建刚,周毅.二氧化碳的腐蚀规律及研究进展[J].甘肃科学学报,2005,17(1):37-40.
【4】王霞,马发明,陈玉祥,等.注CO2提高采收率工程中的腐蚀机理及防护措施[J].钻采工艺,2006,29(6):73-74.
【5】周暐,王 里.均匀设计的原理与应用[J].中国质量,2006(5):47-48.
【2】葛红花,周国定,吴文权.硫离子对316L不锈钢耐蚀性的影响[J].华北电力技术,2003(8):46-49.
【3】周琦,王建刚,周毅.二氧化碳的腐蚀规律及研究进展[J].甘肃科学学报,2005,17(1):37-40.
【4】王霞,马发明,陈玉祥,等.注CO2提高采收率工程中的腐蚀机理及防护措施[J].钻采工艺,2006,29(6):73-74.
【5】周暐,王 里.均匀设计的原理与应用[J].中国质量,2006(5):47-48.
相关信息