工艺参数对锌合金表面化学镀镍速率的影响
Effect of Process Parameters on Deposition Rate of Electroless Nickel Plating on Zinc Alloy
摘 要
采用碱性预镀＋酸性化学镀镍的方法在锌合金表面镀镍,研究了pH值、温度和主要镀液成分对锌合金表面化学镀镍速率的影响,结果表明:在镀液不发生分解时,镀速随pH值和温度的提高而迅速上升;硫酸镍、次亚磷酸钠和主络合剂在镀液中的含量存在极限值,超过此值镀速开始下降.优化工艺条件下镀速可达12 μm/h.
工艺参数
化学镀镍
沉积速率
zinc alloy
process parameter
electroless nickel plating
deposition rate
Abstract
The Ni-P coating on zinc alloy prepared by alkaline pre-nickel plating pluse acidic electroless nickel plating was investigated.The effects of bath temperature,pH value and main bath ingredients on deposition rate were discussed.The results indicated that the deposition rate increased rapidly with increasing bath temperature and pH value as the plating bath was stable.The peak value of deposition rate,i.e.12 μm/h,could be obtained by optimized electroless nickel plating process.
中图分类号 TQ153.1
所属栏目 应用技术
基金项目 甘肃省自然科学基金项目(2007GS04799)
收稿日期 2008/7/26
修改稿日期 2008/9/9
网络出版日期
作者单位点击查看
备注刘红军,博士,副教授.
引用该论文: ZHAN Wen-hua,LIU Hong-jun,LI Ya-min,CAO Chi. Effect of Process Parameters on Deposition Rate of Electroless Nickel Plating on Zinc Alloy[J]. Corrosion & Protection, 2009, 30(8): 561～563
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】唐长斌,刘道新,刘军,等.锌合金压铸件化学镀镍[J].材料保护,2005,38(1):34-36.
【2】胡文彬,刘磊,仵亚婷,等.难镀基材的化学镀镍技术[M].化学工业出版社,2003:75．
【3】梁志杰.现代表面镀覆技术[M].国防工业出版社,2005:377-388．
【4】何向辉,刘彦哲,顾耀前,等.快速光亮化学镀镍工艺[J].电镀与环保,2006,26(2):24-26．
【5】张丕俭,刘艳红,夏振展.低温快速化学镀镍工艺研究[J].电镀与环保,2005,25(2):24-26．
【2】胡文彬,刘磊,仵亚婷,等.难镀基材的化学镀镍技术[M].化学工业出版社,2003:75．
【3】梁志杰.现代表面镀覆技术[M].国防工业出版社,2005:377-388．
【4】何向辉,刘彦哲,顾耀前,等.快速光亮化学镀镍工艺[J].电镀与环保,2006,26(2):24-26．
【5】张丕俭,刘艳红,夏振展.低温快速化学镀镍工艺研究[J].电镀与环保,2005,25(2):24-26．
相关信息