超超临界机组水冷壁高温腐蚀问题的探讨
High Temperature Corrosion of Water Cooling Wall of Extrasupercritical Units
摘 要
介绍了国内首台超超临界机组水冷壁发生高温腐蚀的基本情况.对水冷壁管进行外观检查、金相分析和能谱微区成分分析,结果表明,管子外表面存在高温硫腐蚀,对发生腐蚀的原因作了探讨,并提出了预防措施.
水冷壁
高温腐蚀
预防措施
extrasupercritical(ESC) unit
water cooling wall
high temperature corrosion
prevention measure
Abstract
The basic status of high temperature corrosion of water cooling wall of the first domestic extrasupercritical (ESC) units is introduced.A water cooling wall tube was analyzed by means of macroscopy inspection,metallograpy analysis and EDS.The results showed that there was high temperature sulfur corrosion on outside surface of the water cooling wall tube.The corrosion reasons are discussed,and some prevention measures are presented.
中图分类号 TG172.8 TK224.9
所属栏目 应用技术
基金项目
收稿日期 2008/8/16
修改稿日期 2008/10/6
网络出版日期
作者单位点击查看
备注刘鸿国,高级工程师.
引用该论文: LIU Hong-guo,CAi Hui,TANG Li-ying. High Temperature Corrosion of Water Cooling Wall of Extrasupercritical Units[J]. Corrosion & Protection, 2009, 30(8): 577～578
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】赵虹,魏勇.燃煤锅炉水冷壁烟侧高温腐蚀的机理及影响因素[J].动力工程,2002,22(2):700-1704.
【2】焦庆丰,姚斌,程刚,等.时颂华 大型电站锅炉水冷壁高温腐蚀原因分析与控制[J].湖南电力,2004(2):5-8.
【2】焦庆丰,姚斌,程刚,等.时颂华 大型电站锅炉水冷壁高温腐蚀原因分析与控制[J].湖南电力,2004(2):5-8.
相关信息