埋地管道硬质聚氨酯泡沫防腐保温层失效模式及其故障树分析
Failure Mode and Fault Tree Analysis of Rigid Polyurethane Foam Insulating Layer for Buried Pipelines
摘 要
为明确硬质聚氨酯泡沫塑料防腐保温层的失效机理及失效模式,通过现场调研以及对相关因素进行分析研究,得到了硬质聚氨酯泡沫塑料防腐保温层的主要失效模式:并在此基础上建立了该失效的故障树分析模型,实现了防腐保温层失效的定量化分析.此外,针对导致失效的主要环节,提出了防范硬质聚氨酯泡沫塑料防腐保温层失效的对策.
防腐保温层
失效模式
故障树
防范对策
rigid polyurethane foam
anti-corrosion insulating layer
failure mode
fault tree analysis
countermeasure
Abstract
In order to definite the failure mechanisms and modes of rigid polyurethane foam anti-corrosion heat insulating layer,field investigation and analysis of failure factors were carried out,and the major failure modes were drawn.The model of fault tree analysis(FAT) for rigid polyurethane foam anti-corrosion heat insulating layer was established,which realized quantitative analysis of the failure.For the key links resulting in the failure,some countermeasures are presented.
中图分类号 TG174.46
所属栏目 应用技术
基金项目 国家“十一五”科技支撑计划课题“生命线工程安全保障关键技术研究及工程示范”(项目编号:2006BAK02B01-1)
收稿日期 2008/7/14
修改稿日期 2009/4/5
网络出版日期
作者单位点击查看
联系人作者王新华(dostong@163.com)
备注王新华,教授,博士.
引用该论文: WANG Xin-hua,WANG Tong,HE Ren-yang,MENG Tao. Failure Mode and Fault Tree Analysis of Rigid Polyurethane Foam Insulating Layer for Buried Pipelines[J]. Corrosion & Protection, 2009, 30(9): 660～664
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】刘杰,林荣芳.泡沫夹克防腐蚀保温层的材料选择与结构设计[J].腐蚀与防护,2008,29(2):80-83.
【2】刘冰,张宏.埋地钢质管道沥青外覆盖层保护失效评价概述[J].腐蚀与防护,2006,27(2):90-93,97.
【3】卢子兴.聚氨酯泡沫塑料拉伸本构关系及其失效机理的研究[J].航空学报,2002,3(2):151-154.
【4】Robert T Clmen,Robert L Winter.Combining probability distributions from experts in risk analysis[J].Risk Analysis,1999,19(12):187-203.
【5】金星,洪延姬.工程系统可靠性数值分析方法[M].北京:国防工业出版社,2002:142-146.
【6】SY/T 0415-1996.埋地钢质管道硬质聚氨酯泡沫塑料防腐保温层技术标准[S].
【7】秦国治,丁量棉,田志明.管道防腐蚀技术[M].北京:化学工业出版社,2004.
【8】杨槐安.长输管道施工技术概述[J].化工建设工程,2000,5(22):7-11.
【9】Ahmad Rais.Guided wave technique to detect defects in pipes using wavelet analysis[D].Phoenix:The University of Arizona,2005.
【10】Muhlbauer W Kent.管道风险管理手册[M].杨嘉瑜,张德彦译.北京:中国石化出版社,2005.
【2】刘冰,张宏.埋地钢质管道沥青外覆盖层保护失效评价概述[J].腐蚀与防护,2006,27(2):90-93,97.
【3】卢子兴.聚氨酯泡沫塑料拉伸本构关系及其失效机理的研究[J].航空学报,2002,3(2):151-154.
【4】Robert T Clmen,Robert L Winter.Combining probability distributions from experts in risk analysis[J].Risk Analysis,1999,19(12):187-203.
【5】金星,洪延姬.工程系统可靠性数值分析方法[M].北京:国防工业出版社,2002:142-146.
【6】SY/T 0415-1996.埋地钢质管道硬质聚氨酯泡沫塑料防腐保温层技术标准[S].
【7】秦国治,丁量棉,田志明.管道防腐蚀技术[M].北京:化学工业出版社,2004.
【8】杨槐安.长输管道施工技术概述[J].化工建设工程,2000,5(22):7-11.
【9】Ahmad Rais.Guided wave technique to detect defects in pipes using wavelet analysis[D].Phoenix:The University of Arizona,2005.
【10】Muhlbauer W Kent.管道风险管理手册[M].杨嘉瑜,张德彦译.北京:中国石化出版社,2005.
相关信息