Influence of H2S Partial Pressure on Corrosion Behavior of Super Anti-sulfide Well Tube Steel SM80SS in CO2/H2S Environment
摘 要
用失重法、扫描电镜(SEM)、X射线能谱(EDS)及X射线衍射(XRD)等方法,就H2S分压对SM80SS特级抗硫套管钢在CO2/H2S共存条件下的腐蚀行为的影响进行了试验研究.结果表明:在试验条件下,低PH2S时,以CO2腐蚀为主,腐蚀产物膜由FeS0.9和FeCO3组成,腐蚀产物膜颗粒细小、致密,平均腐蚀速率较低;随着PH2S的增大,反应逐渐变为以H2S为主,FeS0.9逐渐转变为FeS,腐蚀产物膜颗粒粗大、疏松,随后又变得细小、致密,腐蚀速率呈现先增大后逐渐减小的趋势;高PH2S时,FeS的生成较大程度阻碍了FeCO3的生成.腐蚀产物有较好的局部腐蚀阻碍作用,腐蚀形式均为均匀腐蚀.
Abstract
Corrosion behavior of super anti-sulfide well tube steel SM80SS was studied in the CO2/H2S environment.The results showed that CO2 was the major reactant at low PH2S,the corrosion product film consisted of FeS0.9 and FeCO3 was fine and compact,the average corrosion rate was low.As PH2S increased,FeS0.9 was changed to FeS,H2S was the major reactant and the corrosion product film was coarse and loose.when PH2S increased further,the corrosion product film became fine and compact again,average corrosion rate increased firstly and then decreased.FeS could obstruct the formation of FeCO3.Corrosion mode was uniform corrosion.
中图分类号 TG172.82 TG174.2
所属栏目 试验研究
基金项目
收稿日期 2008/10/17
修改稿日期 2008/11/17
网络出版日期
作者单位点击查看
引用该论文: ZHOU Wei-jun,GUO Rui,ZHANG Yong. Influence of H2S Partial Pressure on Corrosion Behavior of Super Anti-sulfide Well Tube Steel SM80SS in CO2/H2S Environment[J]. Corrosion & Protection, 2009, 30(11): 784~786
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】张承中.金属的腐蚀与防护[M].北京:冶金工业出版社,2000:105.
【2】Fierro G,Ingo G M,Mancla Fi.XPS-investigation on the corrosion behavior of 13Cr martensitic stainless steel in CO2-H2S-Cl- environment[J].Corrosion,1989(10):814.
【3】Masamura K,Hashizume S,Sakai J.Polarization behavior of high-Aaloy OCTG in CO2 environment as affected by chlorides and sulfides[J].Corrosion,1987(6):359.
【4】周计明.油管钢在含CO2/H2S高温高压水介质中的腐蚀行为及防护技术的作用[D].西安:西北工业大学硕士学位论文,2002:26.
【5】周卫军,严密林,王成达.N80抗硫油管钢在含CO2、微量H2S及高浓度Cl-腐蚀介质中的腐蚀行为[J].腐蚀科学与防护技术,2007,19(3):192-195.
【2】Fierro G,Ingo G M,Mancla Fi.XPS-investigation on the corrosion behavior of 13Cr martensitic stainless steel in CO2-H2S-Cl- environment[J].Corrosion,1989(10):814.
【3】Masamura K,Hashizume S,Sakai J.Polarization behavior of high-Aaloy OCTG in CO2 environment as affected by chlorides and sulfides[J].Corrosion,1987(6):359.
【4】周计明.油管钢在含CO2/H2S高温高压水介质中的腐蚀行为及防护技术的作用[D].西安:西北工业大学硕士学位论文,2002:26.
【5】周卫军,严密林,王成达.N80抗硫油管钢在含CO2、微量H2S及高浓度Cl-腐蚀介质中的腐蚀行为[J].腐蚀科学与防护技术,2007,19(3):192-195.
相关信息