Influence of Surface Nanocrystallization on Thermal Diffusion of Zn
摘 要
热扩散渗锌过程是一种固态扩散反应,反应时间长、速度慢.表面纳米化技术作为一项新的表面处理技术应用于热扩散渗锌,可以降低渗锌温度和缩短渗锌周期.对表面纳米化处理以及添加剂对渗层厚度、保温时间、保温温度的影响进行了探索性试验.试验表明纳米化层对于扩散更加敏感,时间的影响对于纳米化层并不显著.同时结合其它渗剂的使用,表面纳米层对渗层的改善作用又有所提高,温度越高,渗层厚度增加越明显.
Abstract
Surface nanocrystallization has been used in many aspects as a new way of suface treatment technology,especially in reducing temperature and time of sherardizing.The influence of surface nanocrystallization and additive on the thickness,temperature and time of thermal diffusion was discussed.Experiments showed that the nanocrystallization layer was more sensitive to the diffusion,the effect of time on the nanocrystallizaton layer was not remarkable.By using other additives,the diffusion layer was further improved.
中图分类号 TG174.44 TG178
所属栏目 应用技术
基金项目
收稿日期 2008/11/9
修改稿日期 2008/11/27
网络出版日期
作者单位点击查看
备注张晶,研究生.
引用该论文: ZHANG Jing,YANG Xin-qi. Influence of Surface Nanocrystallization on Thermal Diffusion of Zn[J]. Corrosion & Protection, 2009, 30(11): 837~838
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】顾国成,吴文森.钢铁材料的防蚀涂层[M].北京:科学出版社,1987.
【2】(苏)利亚霍维奇主编.金属和合金的化学热处理手册[M].孙一唐等译,上海:上海科技出版社,1986.
【3】卢燕平,于福洲.渗镀[M].北京:机械工业出版社,1985.
【4】吴勇,李春燕,李立群,等.船舰零部件真空渗锌的性能及应用研究[J].热加工工艺,2002(2):23-25.
【5】许并社.纳米材料及应用技术[M].北京:化学工业出版社,2004.
【6】李雁翔.粉镀(渗)锌技术及其工业应用[J].有色冶炼,1998(1):27-29.
【7】郭庆珍,吴怀隶.钢铁制件防腐蚀新技术-粉末镀锌[J].矿冶,1995,14(2):17-20.
【8】刘志.超音速微粒轰击不锈钢表面纳米化的研究[D].沈阳:中国科学院金属研究所,2001.
【9】王佳杰,霍树斌,王吉孝,等.超音速微粒高能轰击16MnR钢表面纳米化的研究[J].焊接,2006(2):43-46.
【2】(苏)利亚霍维奇主编.金属和合金的化学热处理手册[M].孙一唐等译,上海:上海科技出版社,1986.
【3】卢燕平,于福洲.渗镀[M].北京:机械工业出版社,1985.
【4】吴勇,李春燕,李立群,等.船舰零部件真空渗锌的性能及应用研究[J].热加工工艺,2002(2):23-25.
【5】许并社.纳米材料及应用技术[M].北京:化学工业出版社,2004.
【6】李雁翔.粉镀(渗)锌技术及其工业应用[J].有色冶炼,1998(1):27-29.
【7】郭庆珍,吴怀隶.钢铁制件防腐蚀新技术-粉末镀锌[J].矿冶,1995,14(2):17-20.
【8】刘志.超音速微粒轰击不锈钢表面纳米化的研究[D].沈阳:中国科学院金属研究所,2001.
【9】王佳杰,霍树斌,王吉孝,等.超音速微粒高能轰击16MnR钢表面纳米化的研究[J].焊接,2006(2):43-46.
相关信息