铈盐掺杂GPTMS/TEOS硅烷杂化膜腐蚀电化学行为随时间的变化
Changes of Corrosion Electrochemical Behavior of Cerium Nitrate Doped GPTMS/TEOS Silane Hybrid Films with Immersion Time
摘 要
以γ-环氧丙氧丙基三甲氧基硅烷(GPTMS)和正硅酸乙酯(TEOS)为前躯体,采用溶胶-凝胶法在LY12铝合金基体表面制备了铈盐Ce(NO3)3掺杂有机-无机杂化膜.通过极化曲线与电化学阻抗谱(EIS)研究铈盐掺杂硅烷杂化膜在3.5%(质量分数)NaCl溶液中耐蚀性能随浸泡时间的变化.结果表明,硅烷杂化膜的极化阻抗值随浸泡时间延长而缓慢降低,但浸泡183 h后仍显著高于金属基体;铝合金点蚀电位在浸泡期间呈现先降低后升高再降低的变化.在浸泡初期,EIS曲线的高频容抗行为显著.从69 h至260 h浸泡试验结束,低频阻抗值保持基本稳定.上述变化与膜中掺杂的铈盐具有自修复性质密切相关.
有机硅烷
铝合金
极化曲线
电化学阻抗谱
cerium salt
silane
aluminum alloy
polarization curve
electrochemical impedance spectroscopy
Abstract
Silane-based organic-inorganic hybrid films doped with cerium nitrate were prepared on LY12 aluminum alloy by sol-gel method using γ-glycidoxypropyltrimethoxysilane (γ-GPTMS) and tetraethylorthosilicate (TEOS) as precursors.The evolution of corrosion resistance of the Ce-doped silane-based hybrid coating with immersion time in 3.5% NaCl solution was investigated by polarization curve and electrochemical impedance spectroscopy (EIS) measurements.The results indicated that the polarization resistance values of the Ce-doped silane-based hybrid films decreased slowly with the increase of immersion time,and was still distinctly greater than that of aluminum substrate after 183 h of immersion.The pitting potentials of the Al alloy presented a variation of decreasing,then increasing and finally decreasing during immersion in NaCl solution.In the first period of immersion,the obvious capacitive behavior in high frequency range of EIS could be observed.The low frequency impedance values remained approximately constant in immersion from 69 h to the end of the experiment.The above changes were related to the self-healing ability of cerium salt doped in the silane hybrid films.
中图分类号 TG174.3+6
所属栏目 试验研究
基金项目 国家自然科学基金项目(50871101);江苏省高校自然科学研究指导性项目(YW06005)资助
收稿日期 2009/1/22
修改稿日期 2009/2/22
网络出版日期
作者单位点击查看
联系人作者张金涛(zhangjt@czu.cn)
备注张金涛,副教授,博士.
引用该论文: ZHANG Jin-tao,LI Chun-dong,PAN Liang,HU Ji-ming. Changes of Corrosion Electrochemical Behavior of Cerium Nitrate Doped GPTMS/TEOS Silane Hybrid Films with Immersion Time[J]. Corrosion & Protection, 2009, 30(12): 879～882
被引情况:
【1】张金涛,李春东,壮亚峰,胡吉明, "阳极氧化和硅烷化增强LY12铝合金耐腐蚀性能",腐蚀与防护 32, 340-344(2011)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】Metroke T L,Gandhi J S,Apblett A.Corrosion resistance properties of Ormosil coatings on 2024-T3 aluminum alloy[J].Prog Org Coat,2004,50(4):231-246.
【2】张金涛,潘亮,李春东.LY12铝合金表面硅烷杂化膜的电化学性能研究[J].电镀与涂饰,2008,27(9):22-25.
【3】Palanivel V,Huang Y,van Ooij W J.Effects of addition of corrosion inhibitors to silane films on the performance of AA2024-T3 in a 0.5 M NaCl solution[J].Prog.Org.Coat,2005,53:153-168.
【4】Cabral A M,Trabelsi W,Serra R,et al.The corrosion resistance of hot dip galvanised steel and AA2024-T3 pre-treated with bis-［triethoxysilylpropyl］ tetrasulfide solutions doped with Ce(NO3)3[J].Corrosion Science,2006,48(11):3740-3758.
【5】张金涛,杨春勇,潘亮,等.2A12铝合金表面铈盐掺杂硅烷杂化膜在3.5% NaCl溶液中耐蚀性能的电化学研究[J].金属学报,2008,44(11):1372-1377.
【6】胡吉明,张鉴清,谢德明,等.环氧树脂涂覆LY12铝合金在NaCl溶液中的阻抗模型[J].物理化学学报,2003,19(2):144-149.
【7】曹楚南,张鉴清.电化学阻抗谱导论[M].北京:科学出版社,2002:156-160.
【8】Zhang J T,Hu J M,Zhang J Q,et al.Studies of impedance models and water transport behaviors of polypropylene coated metals in NaCl solution[J].Progress in Organic Coatings,2004,49(4):293-301.
【9】Zhang J T,Hu J M,Zhang J Q,et al.Studies of water transport behavior and impedance models of epoxy-coated metals in NaCl solution by EIS[J].Progress in Organic Coatings,2004,51(2):145-151.
【2】张金涛,潘亮,李春东.LY12铝合金表面硅烷杂化膜的电化学性能研究[J].电镀与涂饰,2008,27(9):22-25.
【3】Palanivel V,Huang Y,van Ooij W J.Effects of addition of corrosion inhibitors to silane films on the performance of AA2024-T3 in a 0.5 M NaCl solution[J].Prog.Org.Coat,2005,53:153-168.
【4】Cabral A M,Trabelsi W,Serra R,et al.The corrosion resistance of hot dip galvanised steel and AA2024-T3 pre-treated with bis-［triethoxysilylpropyl］ tetrasulfide solutions doped with Ce(NO3)3[J].Corrosion Science,2006,48(11):3740-3758.
【5】张金涛,杨春勇,潘亮,等.2A12铝合金表面铈盐掺杂硅烷杂化膜在3.5% NaCl溶液中耐蚀性能的电化学研究[J].金属学报,2008,44(11):1372-1377.
【6】胡吉明,张鉴清,谢德明,等.环氧树脂涂覆LY12铝合金在NaCl溶液中的阻抗模型[J].物理化学学报,2003,19(2):144-149.
【7】曹楚南,张鉴清.电化学阻抗谱导论[M].北京:科学出版社,2002:156-160.
【8】Zhang J T,Hu J M,Zhang J Q,et al.Studies of impedance models and water transport behaviors of polypropylene coated metals in NaCl solution[J].Progress in Organic Coatings,2004,49(4):293-301.
【9】Zhang J T,Hu J M,Zhang J Q,et al.Studies of water transport behavior and impedance models of epoxy-coated metals in NaCl solution by EIS[J].Progress in Organic Coatings,2004,51(2):145-151.
相关信息