Fe-Cr-Ni-Mo合金27-7Mo的抗CO2腐蚀性能
CO2 Corrosion Resistance of Fe-Cr-Ni-Mo Alloy 27-7Mo
摘 要
模拟大庆油田井下的腐蚀环境,使用高温高压釜进行了27-7Mo合金钢的腐蚀试验,并采用SEM、EDS和XPS测试手段对该钢的腐蚀产物膜进行了分析.结果表明:27-7Mo合金钢CO2腐蚀速率在温度120 ℃,压力10 MPa条件下出现极大值,在其余试验条件下均属于轻度腐蚀.27-7Mo钢腐蚀产物膜较薄,有浅的沟渠,整体属于均匀腐蚀.其腐蚀产物膜主要由Cr、Ni、Mo、Fe的氧化物和氢氧化物构成.
27-7Mo
CO2腐蚀
腐蚀产物膜
Fe-Cr-Ni-Mo alloy
27-7Mo
CO2 corrosion
corrosion product film
Abstract
By simulating the corrosion environment of Daqing oilfield,the corrosion experiments of 27-7Mo alloy steels at high temperature and high pressure were carried out,and the corrosion products were analyzed by SEM,EDS and XPS.The results showed that the corrosion rate of 27-7Mo alloy steel was slight,and exhibited a maximum at 120 ℃ and 10 MPa.The corrosion product film of 27-7Mo alloy steel was thin,and mainly composed of oxide and hydroxide of Cr,Ni,Mo and Fe.
中图分类号 TG174.22
所属栏目 试验研究
基金项目 西南石油大学油气藏地质及开发工程国家重点实验室项目(PLN0609)
收稿日期 2008/11/25
修改稿日期 2009/1/9
网络出版日期
作者单位点击查看
备注任强,硕士研究生.
引用该论文: 任强,李春福,荣金仿,崔世华,李雅杰. CO2 Corrosion Resistance of Fe-Cr-Ni-Mo Alloy 27-7Mo[J]. Corrosion & Protection, 2009, 30(12): 889～891
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】Kerman M B,Morshed A.Carbon dioxide corrosion in oil gas product ion-A compendium critical review of corrosion science and engineering[J].Corrosion,2003,59(8):659-683.
【2】赵国仙,严密林,路民旭,等.石油天然气工业中CO2腐蚀的研究进展[J].腐蚀与防护,1998,19(2):51-54.
【3】张学元,王凤平,于海燕,等.二氧化碳腐蚀与防腐对策研究[J].腐蚀与防护,1997,18(3):104-107.
【4】李国敏,李爱魁,郭兴蓬,等.油气田开发中的CO2腐蚀及防治技术[J].材料保护,2003,36(6):1-4.
【5】郑家燊.二氧化碳腐蚀研究现状[J].断块油气田,1996,3(1):62-65.
【6】路民旭,赵新伟,赵国仙,等.油气采集储运中的腐蚀现状及典型案例[J].腐蚀与防护,2003,23(3):36-40.
【2】赵国仙,严密林,路民旭,等.石油天然气工业中CO2腐蚀的研究进展[J].腐蚀与防护,1998,19(2):51-54.
【3】张学元,王凤平,于海燕,等.二氧化碳腐蚀与防腐对策研究[J].腐蚀与防护,1997,18(3):104-107.
【4】李国敏,李爱魁,郭兴蓬,等.油气田开发中的CO2腐蚀及防治技术[J].材料保护,2003,36(6):1-4.
【5】郑家燊.二氧化碳腐蚀研究现状[J].断块油气田,1996,3(1):62-65.
【6】路民旭,赵新伟,赵国仙,等.油气采集储运中的腐蚀现状及典型案例[J].腐蚀与防护,2003,23(3):36-40.
相关信息