Performance Comparision of Passivation Films on Galvanized Steel Treated with Rare-earth Cerium and Lanthanum Salts
摘 要
运用正交试验分别对稀土铈盐和镧盐钝化进行试验,得出该两种稀土盐钝化镀锌钢板的最优参数和工艺条件.醋酸铅点滴试验、盐雾试验、失重试验和电化学交流阻抗谱(EIS)测定表明,镧盐转化膜的耐蚀性优于铈盐转化膜,接近常规铬酸盐转化膜.扫描电镜(SEM)表明,镧盐转化膜明显比铈盐转化膜成膜致密,对基体覆盖度更高,且膜层相对较厚.XRD分析显示,铈盐成膜物质主要是CeO2,镧盐主要是La2O3.漆膜划格试验表明,镧盐转化膜附着力优于铈盐转化膜,达到5B标准,再涂装性能可靠.
Abstract
The optimal processing parameters and conditions of passivation films on galvanized steel sheet treated with rare-earth cerium and lanthanum salts were obtained by orthogonal experimental method.The lead acetate test,salt spray test,weight loss test,EIS,SEM and XRD etc.were used to analyze the performance of passivation films.The results showed that the corrosion resistance of lanthanum film was better than that of cerium film,and the former was more close to the conventional chromate conversion coating.The lanthanum film was more dense and thicker,and had higher coverage on the matrix than cerium film.XRD analysis showed that the main filming materials of cerium salt and lanthanum salt was La2O3 and CeO2 respectively.The adhesion of lanthanum film reached 5B and was better than that of cerium film.
中图分类号 TG178
所属栏目 试验研究
基金项目 中南大学创新项目专项研究基金(ZRE16)
收稿日期 2008/11/26
修改稿日期 2008/12/2
网络出版日期
作者单位点击查看
联系人作者梁永煌(lyh6503@163.com)
备注梁永煌,硕士研究生.
引用该论文: LIANG Yong-huang,MAN Rui-lin,WU Wen-biao. Performance Comparision of Passivation Films on Galvanized Steel Treated with Rare-earth Cerium and Lanthanum Salts[J]. Corrosion & Protection, 2009, 30(12): 892~895
被引情况:
【1】刘小风,曹晓燕, "镀锌钢板钝化工艺研究进展",腐蚀与防护 33, 997-1001(2012)
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】王爱荣,郝海玲.常用镀锌层钝化工艺概述[J].电镀与精饰,2006,28(5):29-31.
【2】单凤君,刘常生,于晓中,等.镀锌钢板无铬钝化技术的研究进展[J].材料保护,2007,40(10):45-48.
【3】林碧兰,卢锦堂,孔纲,等.钼酸盐后处理提高热镀锌上磷化膜耐蚀性的探讨[J].腐蚀与防护,2007,28(8):396-399.
【4】李广超.镀锌层硅酸盐钝化工艺研究[J].电镀与精饰,2007,29(02):31-33.
【5】Kettering A W P,Fairborn J A S,Clayton J T S.Non-toxic corrosion-protection pigments based on rare earth elements: US,7291217 B2[P].2007-11-6.
【6】Huang Xingqiao,Li Ning,Wang Huiyong,et al.Electrodeposited cerium film as chromate replacement for tinplate[J].Thin Solid Films,2008,516:1037-1040.
【7】卢燕平,任玉苓,邱明煊,等.电镀锌钢板涂敷型低铬钝化研究[J].表面技术,1998,27(2):9-11.
【8】颜莎.镀锌钢板稀土铈盐钝化研究[D].长沙:中南大学,2007.
【9】梁永煌.镀锌钢板无铬钝化技术研究[D].长沙:中南大学,2008.
【2】单凤君,刘常生,于晓中,等.镀锌钢板无铬钝化技术的研究进展[J].材料保护,2007,40(10):45-48.
【3】林碧兰,卢锦堂,孔纲,等.钼酸盐后处理提高热镀锌上磷化膜耐蚀性的探讨[J].腐蚀与防护,2007,28(8):396-399.
【4】李广超.镀锌层硅酸盐钝化工艺研究[J].电镀与精饰,2007,29(02):31-33.
【5】Kettering A W P,Fairborn J A S,Clayton J T S.Non-toxic corrosion-protection pigments based on rare earth elements: US,7291217 B2[P].2007-11-6.
【6】Huang Xingqiao,Li Ning,Wang Huiyong,et al.Electrodeposited cerium film as chromate replacement for tinplate[J].Thin Solid Films,2008,516:1037-1040.
【7】卢燕平,任玉苓,邱明煊,等.电镀锌钢板涂敷型低铬钝化研究[J].表面技术,1998,27(2):9-11.
【8】颜莎.镀锌钢板稀土铈盐钝化研究[D].长沙:中南大学,2007.
【9】梁永煌.镀锌钢板无铬钝化技术研究[D].长沙:中南大学,2008.
相关信息