AlFeCoNiCrTiVx系高熵合金的组织结构及电化学性能
Microstructure and Electrochemical Properties of AlFeCoNiCrTiVx High-entropy Alloys
摘 要
研究了不同钒含量的AlFeCoNiCrTiVx(x为摩尔比,x=0.5,1,1.5,2)多主元高熵合金的组织结构及其在0.5 mol/L H2SO4溶液和1 mol/L NaCl溶液中的电化学性能,并与市售304不锈钢进行了对比.结果表明:随着钒元素的添加,合金的组织结构逐渐由两个bcc相组成变为单一的bcc相.极化曲线测试结果表明,在0.5 mol/L H2SO4溶液以及1 mol/L NaCl溶液中,该系合金的耐腐蚀性要明显优于市售304不锈钢,而其中AlFeCoNiCrTiV0.5合金具有最优越的综合耐腐蚀性能.
微观结构
电化学性能
AlFeCoNiCrTiVx high entropy alloy
microstructure
electrochemical property
Abstract
The microstructure and electrochemical properties of equiatomic and high entropy AlFeCoNiCrTiVx (x,molar ratio,x=0.5,1,1.5,2) alloys were investigated in 0.5 mol/L H2SO4 solution and 1 mol/L NaCl solution,and compared with 304 stainless steel.The results showed that the alloy composition was changed from two-bcc phase to a single bcc phase.The polarization curves showed that the alloy system had better corrosion resistance than 304 stainless steel in 0.5 mol/L H2SO4 solution and 1 mol/L NaCl solution,and the AlFeCoNiCrTiV0.5 alloy had the best comprehensive corrosion resistance.
中图分类号 TG174.2
所属栏目 试验研究
基金项目 广西信息材料重点实验室研究基金
收稿日期 2009/7/28
修改稿日期 2009/8/11
网络出版日期
作者单位点击查看
备注罗晓艳,硕士研究生.
引用该论文: LUO Xiao-yan,LIU Gui-zhong,LI Wei,GUO Jing-jie. Microstructure and Electrochemical Properties of AlFeCoNiCrTiVx High-entropy Alloys[J]. Corrosion & Protection, 2010, 31(5): 355～358
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】Yeh J W,Chen S K,Lin S J,et al.Nanostructured high-entropy alloys with multiple principal element[J].Advanced Engineering Material,2004,6(5):299-303.
【2】Swalin R A,E Burke,B Chalmers,et al.In thermodynamics of solids[M].NY:John Wiley,1991:21.
【3】Tong C J,Chen S K,Yeh J W,et al.Microstructure characterization of Alx CoCrCuFeNi high-entropy alloy system with multi-principal lements[J].Metall Mat Trans A,2005(36A):881-893.
【4】陈敏,刘源,李言祥,等.多主元高熵合金AlTiFeNiCuCrx微观结构和力学性能[J].金属学报,2007,43(10):1020-1024.
【5】刘源,李言祥,陈祥,等.多主元高熵合金研究进展[J].材料导报,2006,20(4):4-6.
【6】刘源,陈敏,李言祥. 多主元高熵合金的组织和性能特点[C]//郑州:特种铸造及有色合金年会,2006:252-255.
【7】李伟,刘贵仲,郭景杰.AlxFeCoNiCrTi系高熵合金的组织结构及电化学性能研究[J].铸造,2009,58(5):431-435.
【8】许右睿.FeCoNiCrCux高熵合金之抗蚀性研究[D].台湾:国立台湾海洋大学硕士论文,2004.
【9】童重缙.Cu-Co-Ni-Cr-Al-Fe高熵合金变形结构与高温特性之研究[D].台湾:台湾国立清华大学硕士论文,2002.
【10】陈岳锋.CoCrFrNiTi高乱度合金块材与薄膜性质之研究[D].台湾:台湾私立中国文化大学硕士论文,2004.
【11】梁成浩.金属腐蚀学导论[M].北京:机械工业出版社,1999:72-77.
【2】Swalin R A,E Burke,B Chalmers,et al.In thermodynamics of solids[M].NY:John Wiley,1991:21.
【3】Tong C J,Chen S K,Yeh J W,et al.Microstructure characterization of Alx CoCrCuFeNi high-entropy alloy system with multi-principal lements[J].Metall Mat Trans A,2005(36A):881-893.
【4】陈敏,刘源,李言祥,等.多主元高熵合金AlTiFeNiCuCrx微观结构和力学性能[J].金属学报,2007,43(10):1020-1024.
【5】刘源,李言祥,陈祥,等.多主元高熵合金研究进展[J].材料导报,2006,20(4):4-6.
【6】刘源,陈敏,李言祥. 多主元高熵合金的组织和性能特点[C]//郑州:特种铸造及有色合金年会,2006:252-255.
【7】李伟,刘贵仲,郭景杰.AlxFeCoNiCrTi系高熵合金的组织结构及电化学性能研究[J].铸造,2009,58(5):431-435.
【8】许右睿.FeCoNiCrCux高熵合金之抗蚀性研究[D].台湾:国立台湾海洋大学硕士论文,2004.
【9】童重缙.Cu-Co-Ni-Cr-Al-Fe高熵合金变形结构与高温特性之研究[D].台湾:台湾国立清华大学硕士论文,2002.
【10】陈岳锋.CoCrFrNiTi高乱度合金块材与薄膜性质之研究[D].台湾:台湾私立中国文化大学硕士论文,2004.
【11】梁成浩.金属腐蚀学导论[M].北京:机械工业出版社,1999:72-77.
相关信息