微弧氧化铝合金在海水中的腐蚀行为
Corrosion Behavior of Microarc Oxidation Films on Aluminum Alloy in Seawater
摘 要
采用室内海水浸泡试验、铜离子浸泡试验、电偶试验等方法研究了微弧氧化层和封孔处理对6061铝合金耐海水腐蚀性能的影响.结果显示,微弧氧化后铝合金在海水中的腐蚀形貌为点蚀,封孔处理可明显降低点蚀的发生.与铜合金偶合对微弧氧化铝合金的腐蚀加速较大,在实际使用中应尽量避免两种材料的电接触.
铝合金
腐蚀
海水
microarc oxidation
aluminum alloy
corrosion
seawater
Abstract
In order to study the effect of microarc oxidation and sealing treatment on seawater corrosion resistance of 6061 aluminum alloy,the laboratory seawater immersion test,copper ion solution immersion test and galvanic corrosion test were carried out.The results showed that there was pitting corrosion on microarc oxidized aluminum alloy and the pitting was reduced after sealing treatment.Corrosion of microarc oxidized aluminum alloy was accelerated when it was coupled with copper alloy.The electrical contact of microarc oxidized aluminum alloy with copper alloy should be avoided.
中图分类号 TG172.5
所属栏目 试验研究
基金项目
收稿日期 2009/7/31
修改稿日期 2009/10/19
网络出版日期
作者单位点击查看
备注韩东锐,工程师.
引用该论文: HAN Dong-rui,ZHANG Bo,OU Jia-cai,CHEN Li-jun. Corrosion Behavior of Microarc Oxidation Films on Aluminum Alloy in Seawater[J]. Corrosion & Protection, 2010, 31(6): 452～454
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】刘建平,旷亚非.微弧氧化技术及其发展[J].材料导报,1998,12(5):27-29.
【2】蒋百灵,白力静,蒋永锋,等.铝合金微弧氧化技术[J].西安理工大学学报,2000,16(2):138-142.
【3】李淑华,尹玉军,程金生,等.微弧氧化技术与材料表面陶瓷化[J].特种铸造及有色合金,2001(1):36-37.
【4】薛文斌,华 铭,施修龄,等.铸造铝合金微弧氧化膜的生长动力学及耐蚀性能[J].硅酸盐学报,2007,35(6):731-734.
【5】薛文斌,蒋兴莉,杨卓,等.6061铝合金微弧氧化陶瓷膜的生长动力学及性能分析[J].功能材料,2008,39(4):603-606.
【2】蒋百灵,白力静,蒋永锋,等.铝合金微弧氧化技术[J].西安理工大学学报,2000,16(2):138-142.
【3】李淑华,尹玉军,程金生,等.微弧氧化技术与材料表面陶瓷化[J].特种铸造及有色合金,2001(1):36-37.
【4】薛文斌,华 铭,施修龄,等.铸造铝合金微弧氧化膜的生长动力学及耐蚀性能[J].硅酸盐学报,2007,35(6):731-734.
【5】薛文斌,蒋兴莉,杨卓,等.6061铝合金微弧氧化陶瓷膜的生长动力学及性能分析[J].功能材料,2008,39(4):603-606.
相关信息