NiAl-31Cr-3Mo合金的低温热腐蚀性能
Low Temperature Hot Corrosion Properties of NiAl-31Cr-3Mo Alloy
摘 要
通过对NiAl-31Cr-3Mo合金在550 ℃、600 ℃、650 ℃和700 ℃四种温度下进行恒温热腐蚀试验,研究其低温热腐蚀行为,通过电子显微镜、SEM进行表面观察分析,探讨了NiAl-31Cr-3Mo合金的低温热腐蚀机理.结果表明:NiAl-31Cr-3Mo的热腐蚀存在孕育期,在孕育期间首先形成保护性Al2O3和Cr2O3氧化膜.在550~650 ℃之间,这种保护作用较为明显.最严重的低温热腐蚀发生在650~700 ℃之间,低温热腐蚀后合金表面为坑点状,发生点蚀,并且有贫铬、贫铝现象,这造成Mo含量升高,从而引发酸性腐蚀.
NiAl基合金
低温热腐蚀
点蚀
intermetallics
NiAl-based alloy
low temperature hot corrosion
pitting corrosion
Abstract
The low temperature hot corrosion behavior of NiAl-31Cr-3Mo alloy was investigated under constant temperature condition of 550 ℃,600 ℃,650 ℃ and 700 ℃.The microstructure of NiAl-31Cr-3Mo alloy before and after the low temperature hot corrosion were analyzed by means of optical microscopy(OM),SEM and TEM,and the mechanism of low temperature hot corrosion was discussed.There was an incubation period at the initial stage of hot corrosion.The continuous layers of Al2O3 and Cr2O3 were formed on the surface of NiAl-31Cr-3Mo alloy which provided protective effect at 550~650 ℃.At 650~700 ℃,the hot corrosion became serious,cavities were observed in the alloy surface,indicating pitting corrosion occurred,and the basic condition for the acid corrosion of Al-poor,Cr-poor and Mo-rich phases appeared.
中图分类号 TG172.8
所属栏目 试验研究
基金项目
收稿日期 2009/8/24
修改稿日期 2009/9/23
网络出版日期
作者单位点击查看
联系人作者郜华萍(ynkmghp@263.com)
引用该论文: WU Fei,GAO Hua-ping,ZHANG Guang-ye,LONG Jin-ming,JIE Xing-di. Low Temperature Hot Corrosion Properties of NiAl-31Cr-3Mo Alloy[J]. Corrosion & Protection, 2010, 31(7): 536～539
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】郭建亭.有序金属间化合物镍铝合金[M].北京:科学出版社,2003.
【2】李铁藩.21世纪高温氧化的发展方向[J].材料保护,2000,33(1):12-15.
【3】张光业,张 华,郭建亭.多相NiAl-Cr合金的微观组织与韧脆转变行为的研究[J].材料工程,2005(11):24.
【4】Tolpygo V K,Clark D R,Murphy K S.Oxidation-induced failure of EB-PVD thermal barrier coating[J].Surf Coat Techn,2001,146/147:124-131.
【5】Johnson D R,Chen X F.Processing and mechanical properties of in-situ composites from NiAl-Cr and NiAl-C(Mo) eutectic systems[J].Intermetallics,1995,3(2):99-113.
【6】Whittenbeger J D.Effects of minor alloying additions on the microstructure,toughness and creep strength of directionally solified NiAl-3lCr-3Mo[C]//The third International symposium on structural intermetallics,2001.
【7】徐春梅,郭建亭,杨福宝.NiAl-28Cr-5Mo-1Hf合金的高温氧化行为研究[J].金属学报,2001,37(8):857-860.
【8】Xu C M,Guo J T.Effect of NiAl microcrystalline coating on the high temperature oxidation behavior of NiAl-33.58Cr-0.5Zralloy[J].Corrosion,2002,59(4):350-355.
【9】李云.高温合金的化学性能的研究[D].沈阳:东北大学、中国科学院金属研究所博士学位论文,2004.
【10】曾潮流,张鉴清,沈华清,等.Ni-Al基金属间化合物的热腐蚀[M].国家高新技术新材料领域专家委员会编,先进材料进展.北京:科学出版社,1995.
【11】李猛进.Pd改性铝化物涂层的高温腐蚀行为[D].沈阳:中国科学院金属研究所博士学位论文,2003.
【12】Li M J,Sun X F.Cyclic oxidation behavior of (Ni,Pd) Al coating[J].Surf Coat Techn,2003,167(1):106-111.
【13】Sun Xiaofeng,Xu Huibin.Investigation of the failure mechanism of thermal barrier coating prepared by electron beam physical vapor deposition[J].Surf Coat Techn,2000,130(1):122-127.
【14】杨松岚,王福会.NiAl金属间化合物高温氧化研究进展[J].腐蚀科学与防护技术,2002,14(2):109-112.
【15】张光业.稀土元素对NiAl基共晶合金的结构和性能影响的研究[D].沈阳:中国科学院金属研究所博士学位论文,2004.
【16】张光业,郭建亭,叶恒强.NiAl-30.9Cr-3Mo-0.1Dy合金的微观结构与高温氧化行为[J].航空材料学报,2005,25(4):7-10.
【2】李铁藩.21世纪高温氧化的发展方向[J].材料保护,2000,33(1):12-15.
【3】张光业,张 华,郭建亭.多相NiAl-Cr合金的微观组织与韧脆转变行为的研究[J].材料工程,2005(11):24.
【4】Tolpygo V K,Clark D R,Murphy K S.Oxidation-induced failure of EB-PVD thermal barrier coating[J].Surf Coat Techn,2001,146/147:124-131.
【5】Johnson D R,Chen X F.Processing and mechanical properties of in-situ composites from NiAl-Cr and NiAl-C(Mo) eutectic systems[J].Intermetallics,1995,3(2):99-113.
【6】Whittenbeger J D.Effects of minor alloying additions on the microstructure,toughness and creep strength of directionally solified NiAl-3lCr-3Mo[C]//The third International symposium on structural intermetallics,2001.
【7】徐春梅,郭建亭,杨福宝.NiAl-28Cr-5Mo-1Hf合金的高温氧化行为研究[J].金属学报,2001,37(8):857-860.
【8】Xu C M,Guo J T.Effect of NiAl microcrystalline coating on the high temperature oxidation behavior of NiAl-33.58Cr-0.5Zralloy[J].Corrosion,2002,59(4):350-355.
【9】李云.高温合金的化学性能的研究[D].沈阳:东北大学、中国科学院金属研究所博士学位论文,2004.
【10】曾潮流,张鉴清,沈华清,等.Ni-Al基金属间化合物的热腐蚀[M].国家高新技术新材料领域专家委员会编,先进材料进展.北京:科学出版社,1995.
【11】李猛进.Pd改性铝化物涂层的高温腐蚀行为[D].沈阳:中国科学院金属研究所博士学位论文,2003.
【12】Li M J,Sun X F.Cyclic oxidation behavior of (Ni,Pd) Al coating[J].Surf Coat Techn,2003,167(1):106-111.
【13】Sun Xiaofeng,Xu Huibin.Investigation of the failure mechanism of thermal barrier coating prepared by electron beam physical vapor deposition[J].Surf Coat Techn,2000,130(1):122-127.
【14】杨松岚,王福会.NiAl金属间化合物高温氧化研究进展[J].腐蚀科学与防护技术,2002,14(2):109-112.
【15】张光业.稀土元素对NiAl基共晶合金的结构和性能影响的研究[D].沈阳:中国科学院金属研究所博士学位论文,2004.
【16】张光业,郭建亭,叶恒强.NiAl-30.9Cr-3Mo-0.1Dy合金的微观结构与高温氧化行为[J].航空材料学报,2005,25(4):7-10.
相关信息