火力发电厂凝汽器铜管冲刷腐蚀原因
Erosion Cause of Condenser Copper Tubes in a Thermal Power Plant
摘 要
国内某滨海火力发电厂凝汽器BFe-30-1-1铜管管口发生了大面积的冲刷腐蚀,造成凝汽器长期频繁出现泄漏事故.本工作采用自行设计的动态模拟电化学腐蚀测试试验台,对该厂所使用的铜管在电厂提供的循环水样中进行了冲刷腐蚀试验,同时做了失重试验,对采用阴极保护后铜管的腐蚀速度进行了测量.结果表明,循环水中含砂是造成管口出现大面积冲刷腐蚀的主要原因,发生冲刷腐蚀的部位主要集中在距管口0~150 mm范围内,采用阴极保护能有效降低水中带砂引起的冲刷腐蚀速度.
BFe-30-1-1铜管
冲刷腐蚀
阴极保护
condenser
BFe-30-1-1 copper tube
erosion
cathodic protection
Abstract
The continual leakage of condenser in a seaside power plant was caused by severe erosion in the mouth of pipe of BFe-30-1-1 copper tubes.By using the dynamic simulating electrochemical corrosion device made by ourselves,the changes of flow velocity and corrosion rate in circulating water before and after cathodic protection were studied.The results indicated that erosion was caused primarily by the scouring in the range of 0～150 mm to the mouth of pipe,and could be prevented by cathodic protection.
中图分类号 TG172.2
所属栏目 应用技术
基金项目
收稿日期 2009/8/17
修改稿日期 2009/10/12
网络出版日期
作者单位点击查看
备注邓宇强,工程师.
引用该论文: DENG Yu-qiang,LIN Wei-li,ZHANG Xiang-jin,LONG Guo-jun,YAO Jian-tao,LIU Tao,DANG Zhi-jun. Erosion Cause of Condenser Copper Tubes in a Thermal Power Plant[J]. Corrosion & Protection, 2010, 31(7): 560～561
被引情况:
【1】邓先钦,徐群杰,云虹,潘红涛, "具有超疏水表面的铜及铜合金耐蚀行为研究进展",腐蚀与防护 33, 51-54(2012)
【2】张燕,许立国,刘国强,宋丽莎,侯亚琴,唐新建, "凝汽器管在循环冷却水中的腐蚀评价方法",腐蚀与防护 33, 807-809(2012)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】曹杰玉,宋敬霞,汪德良,等.凝汽器管管腐蚀在线监测装置的研制及其应用研究[J].中国电力,2004,37(4):25-29.
【2】邓宇强,曹杰玉,宋敬霞,等.腐蚀在线监测技术在火力发电厂凝汽器铜管的应用[J].中国电力,2006,39(5):72-74.
【2】邓宇强,曹杰玉,宋敬霞,等.腐蚀在线监测技术在火力发电厂凝汽器铜管的应用[J].中国电力,2006,39(5):72-74.
相关信息