热处理对Ni-Ga-Fe系铁磁形状记忆合金力学及耐蚀性能的影响
Effect of Heat Treatment on Corrosion Resistance and Mechanical Properties of Ni-Ga-Fe Ferromagnetic Shape Memory Alloys
摘 要
研究了热处理对Ni-Ga-Fe系铁磁形状记忆合金耐蚀性能与力学性能的影响.采用电子万能试验机、显微硬度计以及电化学综合测试仪分别测试了Ni-Ga-Fe系合金抗压强度、显微硬度和在3.5% NaCl溶液中的阳极极化曲线.结果表明,室温下铸态Ni53Ga27Fe20合金的耐腐蚀性能最好.经700 ℃,4 h热处理后Ni-Ga-Fe系合金的耐蚀性能下降,抗压强度值增大,显微硬度取决于热处理后合金的显微组织.
铁磁性形状记忆合金
耐蚀性能
力学性能
heat treatment
ferromagnetic shape memory alloy
corrosion resistance
mechanical property
Abstract
The effects of heat treatment at 700 ℃ for 4 h on the corrosion resistance and mechanical properties of Ni-Ga-Fe ferromagnetic shape memory alloys were investigated.Compressive strength and micro-hardness of the alloys were measured by micro hardness tester and multi-function electronic testing machine.The corrosion resistances of the Ni-Ga-Fe alloys before and after the heat treatment was studied by polarization curves in 3.5% NaCl solution.The results showed that the Ni53Ga27Fe20 casting alloys had the highest corrosion resistance at room temperature.The corrosion resistance decreased and the compressive strength increased after the heat treatment of the alloys.Micro hardness of the Ni-Ga-Fe alloys was dependent on the microstructure after the heat treatment.
中图分类号 TG174.3 TG139.6
所属栏目 试验研究
基金项目
收稿日期 2009/12/28
修改稿日期 2010/1/18
网络出版日期
作者单位点击查看
引用该论文: XIA Ming-liu,HAN Cheng-shu,MA Li-qun,DING Yi. Effect of Heat Treatment on Corrosion Resistance and Mechanical Properties of Ni-Ga-Fe Ferromagnetic Shape Memory Alloys[J]. Corrosion & Protection, 2010, 31(10): 772～774
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】陶斌武,李松海,刘建华,等.NiTiNb形状记忆合金管接头的耐蚀性能[J].金属学报,2006,42(1):99-102.
【2】Wuttig M,Li J,Craciunescu C.A new ferromagnetic shape memory alloy system[J].Scripta Materialia,2001(44):2393-2397.
【3】Dearing N,Jenner A G.Magnetic and Magnetoelastic Properties of Melt-Spun Ni-Mn-Ga[J].IEEE Trans.Magn.,2006(42):78-80.
【4】Chernenko V A,Pons J,Cesari E,et al.Transformation behaviour and martensite stabilization in the ferromagnetic Co-Ni-Ga Heusler alloy[J].Scripta Materialia,2004(50):225-229.
【5】Fujita A,Fukamichi K,Gejima F,et al.Magnetic properties and large magnetic-field-induced strains in off-stoichiometric Ni-Mn-Al Heusler alloys[J].Applied Physics Letters,2000(77):3054-3056.
【6】Oikawa K,Ota T,Sutou Y,et al.Magnetic and martensitic phase transformations in a Ni54Ga27Fe19 alloy[J].Materials Transactions,2002(43):2360-2362.
【7】夏明六.Ni-Ga-Fe系铁磁形状记忆合金的阻尼性能[D].南京:南京工业大学硕士论文,2009.
【8】夏明六,马立群,阮爱杰,等.铁磁性形状记忆合金Ni-Ga-Fe-Co的阻尼性能[J].机械工程材料,2009,33(3):50-52.
【2】Wuttig M,Li J,Craciunescu C.A new ferromagnetic shape memory alloy system[J].Scripta Materialia,2001(44):2393-2397.
【3】Dearing N,Jenner A G.Magnetic and Magnetoelastic Properties of Melt-Spun Ni-Mn-Ga[J].IEEE Trans.Magn.,2006(42):78-80.
【4】Chernenko V A,Pons J,Cesari E,et al.Transformation behaviour and martensite stabilization in the ferromagnetic Co-Ni-Ga Heusler alloy[J].Scripta Materialia,2004(50):225-229.
【5】Fujita A,Fukamichi K,Gejima F,et al.Magnetic properties and large magnetic-field-induced strains in off-stoichiometric Ni-Mn-Al Heusler alloys[J].Applied Physics Letters,2000(77):3054-3056.
【6】Oikawa K,Ota T,Sutou Y,et al.Magnetic and martensitic phase transformations in a Ni54Ga27Fe19 alloy[J].Materials Transactions,2002(43):2360-2362.
【7】夏明六.Ni-Ga-Fe系铁磁形状记忆合金的阻尼性能[D].南京:南京工业大学硕士论文,2009.
【8】夏明六,马立群,阮爱杰,等.铁磁性形状记忆合金Ni-Ga-Fe-Co的阻尼性能[J].机械工程材料,2009,33(3):50-52.
相关信息