迪那2气田地面装置的腐蚀防护
Corrosion Protection for Dina 2 Gas field Ground Device
摘 要
通过对迪那2气田腐蚀现状进行汇总分析, 研究了油气管道产生腐蚀的原因; 论证在CO2腐蚀环境中, 油气管道有效的防腐蚀工艺; 提出采用内衬不锈钢复合管或22Cr管材的防腐蚀方法, 对容易发生腐蚀的管段进行腐蚀监测, 掌握腐蚀状况, 及时采取修复或更换措施, 减少腐蚀对油气生产的负面影响。
腐蚀防护
油气处理
CO2 corrosion
corrosion protection
oil and gas processing
Abstract
The corrosion reasons of oil and gas pipelines were studied by analyzing the corrosion status in Dina 2 gas field. The effective anticorrosion methods for the pipelines in CO2 corrosion environment were demonstrated. Using lined stainless steel clad pipe or 22Cr pipe was proposed to prevent corrosion. Corrosion monitoring was carried out to those pipelines which were easy to corrode. Through mastering the corrosion status, repairing and replacing the corroded pipeline timely, the negative impact on oil and gas production caused by corrosion was reduced.
中图分类号 TG174 DOI 10.11973/fsyfh-201508019
所属栏目 应用技术
基金项目
收稿日期 2014/8/11
修改稿日期
网络出版日期
作者单位点击查看
联系人作者潘旭(273931282@qq.com)
备注潘旭(1986-),助理工程师,学士,从事油气田开发相关研究,
引用该论文: PAN Xu,YANG He-yi,WANG Sheng-lei,ZHOU Yong-liang,SUN Han. Corrosion Protection for Dina 2 Gas field Ground Device[J]. Corrosion & Protection, 2015, 36(8): 784
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】陈普信, 纪云岭, 张立奎. 小直径管线高压无气喷涂及无补口防腐蚀技术[J]. 石油工程建设, 2001,27(3): 34-35.
【2】攀三新,郭宏,胡晓元. 管道内防腐蚀现场补口新思路[J]. 石油工程建设,2011,37(1): 59-60.
【3】张永刚,赵忠刚,何超. 油气管道内防腐蚀补口技术研究进展[J]. 管道技术与设备, 2009,17(5): 44-46.
【4】王志文,徐宏,关凯本. 化工设备失效原理与案例分析[M]. 上海: 华东理工大学出版社,2010.
【2】攀三新,郭宏,胡晓元. 管道内防腐蚀现场补口新思路[J]. 石油工程建设,2011,37(1): 59-60.
【3】张永刚,赵忠刚,何超. 油气管道内防腐蚀补口技术研究进展[J]. 管道技术与设备, 2009,17(5): 44-46.
【4】王志文,徐宏,关凯本. 化工设备失效原理与案例分析[M]. 上海: 华东理工大学出版社,2010.
相关信息