轧制变形对Al0.3CoCrFeNi高熵合金显微组织和性能的影响
Effects of Rolling Deformation on Microstructure and Properties of Al0.3CoCrFeNi High-Entropy Alloy
摘 要
采用真空感应熔炼法制备Al0.3CoCrFeNi高熵合金, 对其进行不同变形量(30%, 60%, 90%)的轧制变形, 利用光学显微镜、扫描电镜、X射线衍射仪、显微硬度计、电子拉伸机和电化学方法等研究不同变形量合金的显微组织、力学性能和耐腐蚀性能。结果表明: 铸态Al0.3CoCrFeNi高熵合金具有等轴晶组织, 在轧制过程中晶粒沿着轧制方向被拉长细化, 经90%变形量轧制后形成了纤维状组织; 随变形量的增加, Al0.3CoCrFeNi高熵合金的硬度和强度都得到提高, 但是伸长率却下降; 在质量分数为3.5%的NaCl溶液中, 轧制合金的自腐蚀电流密度较铸态合金的大, 表现出较差的耐蚀性。
轧制
力学性能
腐蚀
high-entropy alloy
rolling
mechanical property
corrosion
Abstract
Al0.3CoCrFeNi high-entropy alloys (HEAs) were prepared by vacuum induction melting and then were rolled at different deformation degrees (30%, 60%, 90%). Microstructure, mechanical property and corrosion resistance property of these HEAs were investigated by OM, SEM, XRD, microhardness testing, tensile testing and electrochemical method. The results show that the grains in cast HEAs exhibited equiaxed, and were elongated along the rolling direction and finally formed fibrous microstructure during rolling. The hardness and strength of HEAs increased with the increase of the deformation degree, but the elongation decreased. In 3.5wt.% NaCl solution, HEAs had higher corrosion current density in rolled state than in cast state, showing lower corrosion resistance.
中图分类号 TG113.12 TG113.25 DOI 10.11973/jxgccl201508011
所属栏目 新材料 新工艺
基金项目 福建省自然科学基金资助项目(2012J01202);福建省教育厅科技项目(JA11179)
收稿日期 2014/2/17
修改稿日期 2015/3/2
网络出版日期
作者单位点击查看
备注黄艺娜(1988-), 女, 福建漳州人, 硕士研究生。
引用该论文: HUANG Yi-na,TANG Qun-hua,DAI Pin-qiang. Effects of Rolling Deformation on Microstructure and Properties of Al0.3CoCrFeNi High-Entropy Alloy[J]. Materials for mechancial engineering, 2015, 39(8): 51～54
黄艺娜,唐群华,戴品强. 轧制变形对Al0.3CoCrFeNi高熵合金显微组织和性能的影响[J]. 机械工程材料, 2015, 39(8): 51～54
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】YEH J W, CHEN S K, LIN S J. Nano-structured high-entropy alloys with multiple principal elements: novel alloy design concepts and outcomes［J］. Advanced Engineering, 2004, 6(5): 299-303.
【2】刘源, 李言祥, 陈祥, 等. 多主元高熵合金研究进展［J］. 材料导报, 2006, 20(4): 4-6.
【3】李伟, 刘贵仲, 罗晓艳, 等. AlxFeCoNiCrTi合金的抗氧化性能及其退火态的组织和硬度［J］. 机械工程材料, 2010, 34(2): 43-46.
【4】TSAI C, CHEN Y, TSAI M, et al. Deformation and annealing behaviors of high-entropy alloy Al0.5CoCrCuFeNi［J］. Journal of Alloys and Compounds, 2009, 486(1/2): 427-435.
【5】范太云, 唐群华, 陈文哲, 等. 塑性变形对Al0.5FeCoCrNi高熵合金组织结构和性能的影响［J］. 材料科学与工程学报, 2013,31(02): 258-263.
【6】姜传海, 杨传铮. X射线衍射技术及其应用［M］. 上海: 华东理工大学出版社, 2010.
【7】ZHANG Y, ZHOU Y J. Solid Solution formation criteria for high entropy alloys［J］. Materials Science Forum, 2007, 561/565: 1337-1339.
【8】温丽华, 寇宏超, 王一川, 等. AlxCoCrCuFeNi多主元高熵合金的组织与力学性能［J］. 特种铸造及有色合金, 2009, 29(6): 579-581.
【9】SHUN T, HUNG C, LEE C. Formation of ordered/disordered nanoparticles in FCC high entropy alloys［J］. Journal of Alloys and Compounds, 2010, 493(1/2): 105-109.
【10】PAUL H, DRIVER J H, MAURICE C, et al. The role of shear banding on deformation texture in low stacking fault energy metals as characterized on model Ag crystals［J］. Acta Materialia, 2007, 55(2): 575-588.
【11】梅俊, 刘新华, 姜雁斌, 等. 轴向取向组织BFe10-1-1管材冷轧加工过程中组织、织构与力学性能的变化［J］. 中国有色金属学报, 2012, 22(9): 2529-2538.
【12】DE BOOM F R, MATTENS W C M, MIEDEMA A R, et al. Cohesion in Metals ［M］. ［S.l.］: Elsevier Science Publishing Company, 1989.
【13】苏丽凤, 彭开萍, 肖林钢. 反复模压变形法细化H62黄铜的研究［J］. 机械工程材料, 2007, 31(7): 15-18.
【14】任伟才, 彭国胜, 陈康华, 等. 轧制变形量对 Al-Zn-Mg-Cu 合金组织与力学性能以及腐蚀性能的影响［J］. 粉末冶金材料科学与工程, 2013, 18(6): 807-813.
【15】史一功, 张铁邦, 寇宏超, 等. AlCoCrFeNiCu高熵合金的电化学腐蚀性能研究［J］. 热加工工艺, 2011,40(18): 1-3.
【16】李伟, 刘贵仲, 郭景杰. AlFeCuCoNiCrTix高熵合金的组织结构及电化学性能［J］. 特种铸造及有色合金, 2009, 29(10): 941-944.
【2】刘源, 李言祥, 陈祥, 等. 多主元高熵合金研究进展［J］. 材料导报, 2006, 20(4): 4-6.
【3】李伟, 刘贵仲, 罗晓艳, 等. AlxFeCoNiCrTi合金的抗氧化性能及其退火态的组织和硬度［J］. 机械工程材料, 2010, 34(2): 43-46.
【4】TSAI C, CHEN Y, TSAI M, et al. Deformation and annealing behaviors of high-entropy alloy Al0.5CoCrCuFeNi［J］. Journal of Alloys and Compounds, 2009, 486(1/2): 427-435.
【5】范太云, 唐群华, 陈文哲, 等. 塑性变形对Al0.5FeCoCrNi高熵合金组织结构和性能的影响［J］. 材料科学与工程学报, 2013,31(02): 258-263.
【6】姜传海, 杨传铮. X射线衍射技术及其应用［M］. 上海: 华东理工大学出版社, 2010.
【7】ZHANG Y, ZHOU Y J. Solid Solution formation criteria for high entropy alloys［J］. Materials Science Forum, 2007, 561/565: 1337-1339.
【8】温丽华, 寇宏超, 王一川, 等. AlxCoCrCuFeNi多主元高熵合金的组织与力学性能［J］. 特种铸造及有色合金, 2009, 29(6): 579-581.
【9】SHUN T, HUNG C, LEE C. Formation of ordered/disordered nanoparticles in FCC high entropy alloys［J］. Journal of Alloys and Compounds, 2010, 493(1/2): 105-109.
【10】PAUL H, DRIVER J H, MAURICE C, et al. The role of shear banding on deformation texture in low stacking fault energy metals as characterized on model Ag crystals［J］. Acta Materialia, 2007, 55(2): 575-588.
【11】梅俊, 刘新华, 姜雁斌, 等. 轴向取向组织BFe10-1-1管材冷轧加工过程中组织、织构与力学性能的变化［J］. 中国有色金属学报, 2012, 22(9): 2529-2538.
【12】DE BOOM F R, MATTENS W C M, MIEDEMA A R, et al. Cohesion in Metals ［M］. ［S.l.］: Elsevier Science Publishing Company, 1989.
【13】苏丽凤, 彭开萍, 肖林钢. 反复模压变形法细化H62黄铜的研究［J］. 机械工程材料, 2007, 31(7): 15-18.
【14】任伟才, 彭国胜, 陈康华, 等. 轧制变形量对 Al-Zn-Mg-Cu 合金组织与力学性能以及腐蚀性能的影响［J］. 粉末冶金材料科学与工程, 2013, 18(6): 807-813.
【15】史一功, 张铁邦, 寇宏超, 等. AlCoCrFeNiCu高熵合金的电化学腐蚀性能研究［J］. 热加工工艺, 2011,40(18): 1-3.
【16】李伟, 刘贵仲, 郭景杰. AlFeCuCoNiCrTix高熵合金的组织结构及电化学性能［J］. 特种铸造及有色合金, 2009, 29(10): 941-944.
相关信息