Effects of Anodic Oxidation of Carbon Fibers on Mechanical Properties of Carbon/Epoxy Composites
摘 要
利用真空浸渍法制得碳纤维增强环氧复合材料,研究了阳极氧化处理前后碳纤维表面状态的变化及表面处理对复合材料力学性能的影响.结果表明:适当的阳极氧化处理使复合材料的弯曲和剪切性能有很大改善,但冲击性能有所降低.
Abstract
An epoxy-based composite reinforced with carbon fibers (C/EP) was prepared by vacuum impregnation process.The specific surface area and tensile fracture load of carbon fibers were determined after anodic oxidation treatment,and the effects of fibers surface treatment on mechanical properties of C/EP composites were also discussed.The anodic oxidation resulted in the reduction of fibers tensile strength,the larger the current density and the longer the oxidation time,the more the loss.The specific surface area of carbon fibers increased with the oxidation time when the current density was 2A/m2 and initially increased then decreases at 1A/m2.The flexural and shear properties of the C/EP composites with properly oxidized fibers were greatly improved,while the impact strength falled to some extent.Its believed that the interface adhesion of the C/EP composite could be enhanced by the anodic oxidation treatment of carbon fibers,but the oxidation time should not exceed 2 minute in order to obtain a better general mechanical performance.
中图分类号 TB332
所属栏目
基金项目
收稿日期 2004/9/17
修改稿日期 2005/3/1
网络出版日期
作者单位点击查看
备注王玉果(1975-),女,河北石家庄人,副教授,博士.
引用该论文: WANG Yu-guo,WANG Yu-lin,HU Feng-hua. Effects of Anodic Oxidation of Carbon Fibers on Mechanical Properties of Carbon/Epoxy Composites[J]. Materials for mechancial engineering, 2006, 30(1): 53~55
王玉果,王玉林,胡丰华. 阳极氧化对碳/环氧复合材料力学性能的影响[J]. 机械工程材料, 2006, 30(1): 53~55
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】宋焕成,赵时熙.聚合物基复合材料[M].北京:国防工业出版社,1986.
【2】Fukunaga A,Ueda S,Nagumo M.Air-oxidation and anodization of pitch-based carbon fibers[J].Carbon,1999,37(7):1081-1085.
【3】Fukunaga A,Ueda S,Nagumo M.Plasma treatment of pitch-based ultra high modulus carbon fibers[J].Carbon,1999,37(7):1087-1091.
【4】Yue Z R,Jiang W,Wang L,et al.Surface characterization of electrochemically oxidized carbon fibers[J].Carbon,1999,37(11):1785-1796.
【5】杨永岗,贺 福.XRD对表面处理碳纤维表面结构的分析[J].炭素,1998,(3):17-20.
【2】Fukunaga A,Ueda S,Nagumo M.Air-oxidation and anodization of pitch-based carbon fibers[J].Carbon,1999,37(7):1081-1085.
【3】Fukunaga A,Ueda S,Nagumo M.Plasma treatment of pitch-based ultra high modulus carbon fibers[J].Carbon,1999,37(7):1087-1091.
【4】Yue Z R,Jiang W,Wang L,et al.Surface characterization of electrochemically oxidized carbon fibers[J].Carbon,1999,37(11):1785-1796.
【5】杨永岗,贺 福.XRD对表面处理碳纤维表面结构的分析[J].炭素,1998,(3):17-20.
相关信息