滑动对GCr15钢磨损行为的影响
Wear of GCr15 Steel in Coupling of Rolling and Sliding
摘 要
为了研究滑动对GCr15钢磨损失效行为的影响,在M-2000型摩擦磨损试验机上分别进行了纯滚动和滚动与滑动耦合的摩擦磨损试验,用表面粗糙度仪测量了试样在不同磨损阶段的表面形貌,用称重法测量其磨损量.结果表明：在滚动与滑动耦合作用下,GCr15的磨损规律及磨损机理比较复杂,氧化层剥落和点蚀是其主要的磨损形式,温度对GCr15钢磨损影响显著.
GCr15
磨损
sliding
GCr15
wear
Abstract
In order to investigate the behavior of metals wear in coupling of rolling and sliding,GCr15 steels frictional wear was studied using an M2000 experiment machine,by measurring the roughness of surface,and mass.It was found that the mechanism of abrasion in the coupling of rolling and gliding was very complicated.The temperature was a dominating factor of GCr15 steels wear.
中图分类号 TG115.5
所属栏目
基金项目 江苏省自然科学基金资助项目(BK2002116)
收稿日期 2005/4/21
修改稿日期 2005/6/25
网络出版日期
作者单位点击查看
备注王勇华(1981-),男,江苏泰州人,硕士研究生.
引用该论文: WANG Yong-hua,ZHU Hua,WU Zhao-hong,LI Gang. Wear of GCr15 Steel in Coupling of Rolling and Sliding[J]. Materials for mechancial engineering, 2006, 30(6): 23～25
王勇华,朱华,吴兆宏,李刚. 滑动对GCr15钢磨损行为的影响[J]. 机械工程材料, 2006, 30(6): 23～25
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】余小燕,朱华,葛世荣,等.振动轴承磨损失效与对策研究[J].矿山机械,2003,31(3):45-47.
【2】宋期,张人佶.GCr15钢球/Cr7C3涂层盘摩擦副在大气与真空中摩擦学性能的比较[J].摩擦学学报,1993,12(4):15-18.
【3】于翔,王成彪,孙晓军.9Cr18和GCr15球-盘摩擦副摩擦学性能分析[J].材料热处理学报,2002,23(4):47-50.
【4】Leggoe J W,Mammoli A A,Bush M B,et al.Finiteelement modeling of deformation in particulate reinforced metal matrix composites:fiber reinforcement and lamellar inclusions[J].Acta Mater,1998,46(17):6075-6088.
【5】陈洁,熊翔,姚萍屏,等.摩擦面温度对铁基摩擦材料摩擦磨损性能影响机理的研究[J].粉末冶金技术,2004,22(4):223-227.
【2】宋期,张人佶.GCr15钢球/Cr7C3涂层盘摩擦副在大气与真空中摩擦学性能的比较[J].摩擦学学报,1993,12(4):15-18.
【3】于翔,王成彪,孙晓军.9Cr18和GCr15球-盘摩擦副摩擦学性能分析[J].材料热处理学报,2002,23(4):47-50.
【4】Leggoe J W,Mammoli A A,Bush M B,et al.Finiteelement modeling of deformation in particulate reinforced metal matrix composites:fiber reinforcement and lamellar inclusions[J].Acta Mater,1998,46(17):6075-6088.
【5】陈洁,熊翔,姚萍屏,等.摩擦面温度对铁基摩擦材料摩擦磨损性能影响机理的研究[J].粉末冶金技术,2004,22(4):223-227.
相关信息