Effect of Cold Deformation Followed Aging on the Microstructure and Mechanical Properties of Ni36CrTiAl Alloy
摘 要
研究了Ni36CrTiAl合金冷轧后经650,670,700和720 ℃时效以及950 ℃固溶再进行650 ℃时效处理对组织与性能的影响.结果表明:随冷变形后时效温度的升高,胞状γ′相长大明显,650 ℃时效后胞状γ′相的直径为30~60 nm,720 ℃时效后为60~140 nm;冷变形后时效析出的胞状γ′相比固溶后时效析出的数量多,尺寸大;冷变形后时效合金的强度和塑性随时效温度的升高而下降;固溶时效后的抗拉强度和屈服强度分别比冷变形时效降低了26.2%和45.3%,但断后伸长率却增加了1.2倍.
Abstract
The microstructure and properties of Ni36CrTiAl alloy after aging at 650,670,700 and 720 ℃ after cold rolling and aging at 650 ℃ after solid solution at 950 ℃ were studied.The size of cell-shaped γ′ phase increased with increasing the aging temperature after cold rolling,the diameter of cell-shaped γ′ at 650 ℃ aging was about 30-60 nm and that at 720 ℃ was about 60-140 nm.The amount of cell-shaped γ′ after cold rolling followed aging was more than that after solid solution followed aging and the size of the former was also bigger than the latter.The strength and plasticity of Ni36CrTiAl alloy after cold rolling followed aging decreased with increasing the aging temperature.The tensile strength and yield strength of solid solution followed aging was 26.2% and 45.3% less than that of cold rolling followed aging respectively,but the elongation of the former increased 1.2 times of the latter.
中图分类号 TG142.75
所属栏目
基金项目
收稿日期 2005/8/4
修改稿日期 2005/10/20
网络出版日期
作者单位点击查看
备注王立民(1971-),男,辽宁鞍山人,工程师,博士.
引用该论文: WANG Li-min,CHENG Shi-chang,YANG Gang,LIU Zheng-dong,LIN Zhao-jie,BAO Han-sheng. Effect of Cold Deformation Followed Aging on the Microstructure and Mechanical Properties of Ni36CrTiAl Alloy[J]. Materials for mechancial engineering, 2006, 30(9): 4~6
程世长,杨钢,刘正东,林肇杰,包汉生. 冷变形时效对Ni36CrTiAl合金组织与力学性能的影响[J]. 机械工程材料, 2006, 30(9): 4~6
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】陈复民,李国俊,苏德达.弹性合金[M].上海:上海科学技术出版社,1983.315-325.
【2】Bol’shakov A P,Golubev V K,Stepanov S I.Influnce of the initial state of 36NKhTYu alloy on its mechanical properties and failure in dynamic tension[J].Russian Metallurgy,1998,(5):51-54.
【3】程贻举.弹性合金的高温时效行为[J].仪表材料,1990,21(6):355-359.
【4】程贻举,徐其昆,何敏.Ni36CrTiAl弹性合金晶界不连续析出相变动力学的研究[J].功能材料,1993,24(4):368-374.
【5】冯家述,程贻举.Ni36CrTiAl弹性合金700 ℃时效组织的电镜观察[J].功能材料,1991,22(1):51-53.
【6】董明水,孙爱俊,迟永祥,等.CuCoBeTiZr合金强化工艺与组织性能研究[J].金属热处理,2003,28(8):23-27.
【7】苏娟华,董企铭,刘平,等.Cu-0.3Cr-0.15Zr-0.05Mg合金形变时效强化与再结晶[J].金属热处理,2004,29(2):18-21.
【2】Bol’shakov A P,Golubev V K,Stepanov S I.Influnce of the initial state of 36NKhTYu alloy on its mechanical properties and failure in dynamic tension[J].Russian Metallurgy,1998,(5):51-54.
【3】程贻举.弹性合金的高温时效行为[J].仪表材料,1990,21(6):355-359.
【4】程贻举,徐其昆,何敏.Ni36CrTiAl弹性合金晶界不连续析出相变动力学的研究[J].功能材料,1993,24(4):368-374.
【5】冯家述,程贻举.Ni36CrTiAl弹性合金700 ℃时效组织的电镜观察[J].功能材料,1991,22(1):51-53.
【6】董明水,孙爱俊,迟永祥,等.CuCoBeTiZr合金强化工艺与组织性能研究[J].金属热处理,2003,28(8):23-27.
【7】苏娟华,董企铭,刘平,等.Cu-0.3Cr-0.15Zr-0.05Mg合金形变时效强化与再结晶[J].金属热处理,2004,29(2):18-21.
相关信息