Study on Hot Deformation Behavior of TA15 Alloy
摘 要
用Gleeble-1500型热模拟试验机对TA15合金进行了变形温度为650~1 000 ℃、应变速率为0.001~1s-1的热压缩试验,研究了工艺参数对流变应力及组织的影响,计算了应力速率敏感指数m及变形激活能Q,建立了本构方程.结果表明:流变应力随变形温度升高而降低,随应变速率提高而增大;应力速率敏感指数m随变形温度的升高而增大.650~850 ℃时变形激活能为386.32 kJ/mol,850~1 000 ℃时为479.365 kJ/mol,预示在不同的温度区间具有不同的变形机制.
Abstract
The high temperature compression tests of TA15 alloy were carried on Gleeble-1500 simulator.The temperature is from 650 ℃ to 1 000 ℃.The strain rate is from 0.001 s-1 to 1 s-1.The influence of processing parameters on the flow stress and the microstructure was studied.The strain rate sensitivity m and deformation activation energy Q were calculated.And the constitutive equation was presented.The results show that the flow stress decreases with the increase of temperature,while increases with the increase of strain rate.The value of m increases with the increase of deformation temperature.The deformation activation energy Q is 386.320 kJ/mol at 650-850 ℃ and 479.365 kJ/mol at 850-1 000 ℃,which means the two temperature ranges correspond to different deformation mechanism.
中图分类号 TG146.2
所属栏目
基金项目
收稿日期 2005/10/17
修改稿日期 2006/10/15
网络出版日期
作者单位点击查看
备注王洋(1978-),男,黑龙江哈尔滨人,博士研究生.
引用该论文: WANG Yang,YOU Feng-hai,ZHU Jing-chuan,LAI Zhong-hong,LIU Yong. Study on Hot Deformation Behavior of TA15 Alloy[J]. Materials for mechancial engineering, 2006, 30(11): 63~65
王洋,尤逢海,朱景川,来忠红,刘勇. TA15合金热变形行为研究[J]. 机械工程材料, 2006, 30(11): 63~65
被引情况:
【1】张开国,卢俊,缪竹骏,吴元彪,吕维洁,宋洪伟, "Inconel 690合金的高温拉伸变形行为",机械工程材料 35, 16-19(2011)
【2】董显娟,鲁世强,王克鲁,方军,吴超, "基于Murty判据的粗片层状TA15钛合金β相区锻造工艺参数优化",机械工程材料 33, 67-71(2009)
【3】贾元伟, "2507双相不锈钢模拟焊接热影响区的组织与性能",理化检验-物理分册 50, 417-420(2014)
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】舒滢,曾卫东,周军,等.BT20合金高温变形行为的研究[J].材料科学与工艺,2005,13(1):55-58.
【2】徐文臣,单德彬,李春峰,等.TA15合金的动态热压缩行为及其机理研究[J].航空材料学报,2005,25(4):13-19.
【3】洪 权,张振祺.Ti-6Al-2Zr-1Mo-1V合金的热变形行为[J].航空材料学报,2001,21(1):10-12.
【4】曾卫东,胡鲜红,俞汉清,等.Ti-17合金高温变形机理研究[J].材料工程,1996,9:27-30.
【5】熊爱明,陈胜晖,黄维超,等.TC6钛合金的高温变形行为及组织演变[J].稀有金属材料与工程,2003,32(6):447-450.
【6】Seeshacharyulu T,Medeiros S C,Frazier W G,et al.Hot working of commercial Ti-Al-4V with an equiaxed α-β microstructure:materials modeling considerations[J].Materials Science and Engineering,2000,A284:184-194.
【7】Pu Z J,Wu K H,Shi J,et al.Development of constitutive relationships for the hot deformation of boron microalloying TiAl-Cr-V alloys[J].Materials Science and Engineering,1995,A192-193:780-787.
【8】Whittenberger J D.The influence of grain size and composition on slow plastic flow in Fe-Al between 1100 and 1400K[J].Materials Science and Engineering,1986,77:103-106.
【9】冯艾寒.Si3N4/4032Al复合材料高温压缩变形行为研究[D].哈尔滨:哈尔滨工业大学,2005.
【10】冯 亮,曲恒磊,赵永庆,等.TC21合金的高温变形行为[J].航空材料学报,2004,24(4):11-13.
【11】Philippart I,Pack H J.High temperature dynamic yielding in metastable Ti-6.8Mo-4.5F-1.5Al[J].Materials Science and Engineering,1998,A243:196-200.欢迎来稿欢迎订阅欢迎刊登广告(下转第页)
【2】徐文臣,单德彬,李春峰,等.TA15合金的动态热压缩行为及其机理研究[J].航空材料学报,2005,25(4):13-19.
【3】洪 权,张振祺.Ti-6Al-2Zr-1Mo-1V合金的热变形行为[J].航空材料学报,2001,21(1):10-12.
【4】曾卫东,胡鲜红,俞汉清,等.Ti-17合金高温变形机理研究[J].材料工程,1996,9:27-30.
【5】熊爱明,陈胜晖,黄维超,等.TC6钛合金的高温变形行为及组织演变[J].稀有金属材料与工程,2003,32(6):447-450.
【6】Seeshacharyulu T,Medeiros S C,Frazier W G,et al.Hot working of commercial Ti-Al-4V with an equiaxed α-β microstructure:materials modeling considerations[J].Materials Science and Engineering,2000,A284:184-194.
【7】Pu Z J,Wu K H,Shi J,et al.Development of constitutive relationships for the hot deformation of boron microalloying TiAl-Cr-V alloys[J].Materials Science and Engineering,1995,A192-193:780-787.
【8】Whittenberger J D.The influence of grain size and composition on slow plastic flow in Fe-Al between 1100 and 1400K[J].Materials Science and Engineering,1986,77:103-106.
【9】冯艾寒.Si3N4/4032Al复合材料高温压缩变形行为研究[D].哈尔滨:哈尔滨工业大学,2005.
【10】冯 亮,曲恒磊,赵永庆,等.TC21合金的高温变形行为[J].航空材料学报,2004,24(4):11-13.
【11】Philippart I,Pack H J.High temperature dynamic yielding in metastable Ti-6.8Mo-4.5F-1.5Al[J].Materials Science and Engineering,1998,A243:196-200.欢迎来稿欢迎订阅欢迎刊登广告(下转第页)
相关信息