2A50铝合金钎焊钎料与钎剂的选择
The Selection of Filler Metal and Flux for 2A50 Al Alloy Brazing
摘 要
针对2A50铝合金的特点,根据铺展性、填缝性试验,对适合其钎焊的钎料与钎剂作了选择,进行了接头强度试验.结果表明:中温CsF-AlF3钎剂具有较高的活性及较好的去膜效果,适合含镁热处理强化型铝合金的钎焊;用CsF-AlF3钎剂分别与Al-Cu-Ag-Zn钎料及Zn-Al-Be钎料匹配钎焊,均可获得较理想的钎焊效果;当搭接间隙为0.2 mm、搭接长度为2.3 mm时,Zn-Al-Be钎料与CsF-AlF3钎剂匹配钎焊,所得焊接接头的抗剪强度可达143.2 MPa.
钎焊
钎料
钎剂
aluminum alloy
brazing
filler metal
flux
Abstract
The filler metals and fluxes suitabled for 2A50 aluminum alloy brazing were selected according to the feature of 2A50 aluminum alloy and the test of spreadability and clearance fillabitity.Shear tests after the selection indicate that mesothermal CsF-AlF3 flux with high activity and good ability of removing oxide film is appropriate for brazing heat treatment strengthened aluminum alloys containing magnesium element.Adopting CsF-AlF3 flux matched with Al-Cu-Ag-Zn and Zn-Al-Be filler metals respectively obtain good results for brazing 2A50 aluminum alloy.Matching Zn-Al-Be filler metal with CsF-AlF3 flux for brazing 2A50 aluminum alloy could make the shearing strength reach to 143.2 MPa when the lap gap and the lap length are 0.2 mm and 2.3 mm separately.
中图分类号 TG454 TG425
所属栏目
基金项目
收稿日期 2005/12/1
修改稿日期 2006/3/3
网络出版日期
作者单位点击查看
备注鲍俊娟(1978-),女,江苏连云港人,硕士研究生.
引用该论文: BAO Jun-juan,GAO Zhi-guang,LI Chuan,SHENG Qiao-ling,HAN Yi-sheng,QI Kai,WANG Hai-long. The Selection of Filler Metal and Flux for 2A50 Al Alloy Brazing[J]. Materials for mechancial engineering, 2006, 30(12): 40～43
鲍俊娟,高志广,李川,沈巧玲,韩逸生,祈凯,王海龙. 2A50铝合金钎焊钎料与钎剂的选择[J]. 机械工程材料, 2006, 30(12): 40～43
被引情况:
【1】刘树英,刘亚洲,李武会,张冬冬,毛钟泉,鈴村暁男, "普通与急冷Al-Si-Zn钎料的显微组织与力学性能",机械工程材料 40, 44-48(2016)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】周振丰.焊接冶金学[M].北京:机械工业出版社,1996.125-135.
【2】邹僖.钎焊[M].北京:机械工业出版社,1997.101-112.
【3】王祝堂.铝材及其表面处理手册[M].南京:江苏科学技术出版社,1993.120-130.
【4】张启运,庄鸿寿.钎焊手册[M].北京:机械工业出版社,1998.25-69.
【2】邹僖.钎焊[M].北京:机械工业出版社,1997.101-112.
【3】王祝堂.铝材及其表面处理手册[M].南京:江苏科学技术出版社,1993.120-130.
【4】张启运,庄鸿寿.钎焊手册[M].北京:机械工业出版社,1998.25-69.
相关信息